Bulk Molding Compounds BMC 1412 Flame and Track Resistant
| Category | Polymer , Thermoset , Polyester, TS |
| Manufacturer | BMC - Bulk Molding Compounds Inc. |
| Trade Name | BMC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Bulk Molding Compounds BMC 1412 Flame and Track Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
BMC 1412 is an extremely versatile material. Flame and track resistant, low shrink for close dimensional control and surface smoothness, high physical properties. Developed for injection molding, but also suitable for compression or transfer applications. BMC 1412 is approved for Mil specifications, MAI-30, MAI-60 and MAT-30. UL® recognized. This material was formerly known as Glastic® 1412.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.75 - 1.80 g/cc | 1.75 - 1.80 g/cc | |
| Water Absorption | 0.12 - 0.18 % | 0.12 - 0.18 % | 24 hours, 23°C |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Barcol | 40 - 50 | 40 - 50 | |
| Tensile Strength, Ultimate | 41.4 - 48.3 MPa | 6000 - 7000 psi | |
| Flexural Strength | 159 - 172 MPa | 23000 - 25000 psi | |
| Flexural Modulus | 13.1 - 13.8 GPa | 1900 - 2000 ksi | |
| Compressive Strength | 165 - 179 MPa | 24000 - 26000 psi | |
| Izod Impact, Notched | 4.27 - 4.81 J/cm | 8.00 - 9.00 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | >= 260 °C | >= 500 °F | |
| UL RTI, Electrical | 160 °C | 320 °F | |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 19.3 kV/mm | 490 kV/in | Short Time |
| Dissipation Factor | 0.018 @Frequency 60 Hz |
0.018 @Frequency 60 Hz |
Condition A |
| 0.023 @Frequency 60 Hz |
0.023 @Frequency 60 Hz |
Condition A | |
| 0.039 @Frequency 60 Hz |
0.039 @Frequency 60 Hz |
Condition D | |
| 0.152 @Frequency 60 Hz |
0.152 @Frequency 60 Hz |
Condition D | |
| Arc Resistance | 192 sec | 192 sec |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Mold Temperature | 138 - 166 °C | 280 - 330 °F |