Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 6.89 - 50.0 MPa | 1000 - 7250 psi | Average value: 20.3 MPa Grade Count:68 |
Overview of materials for Polytetrafluoroethylene (PTFE), Glass Filled, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Glass Filled, Molded". Each property range of values reported is minimum.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | molded-without post cure; ASTM D412 |
Multibase C6-235 PERKADOX PD-50S Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | molded-without post cure; ASTM D412 |
Multibase C6-235 VAROX DBPH Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Sylvin Technologies 8980-60 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Sylvin Technologies 8999-65 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Sylvin Technologies 9980-60 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Sylvin Technologies 9999-65 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | Dry; ASTM D412 |
Lubrizol Estane® ALR G500 Water Absorbent Thermoplastic Polyurethane Type: Estane® ALR G500 is an aliphatic thermoplastic polyurethane (TPU) resin designed to absorb water and transport moisture.Features: Contains UV additivesAvailable in AmericasInformation Provide.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Dow Corning SILASTIC® 37084-D SILICONE RUBBER BLACK 40 Durometer, peroxide cured, low compression set Silicone Rubber CompoundInformation provided by Dow Corning |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Dow Corning SILASTIC® S RTV SILICONE RUBBER BASE & GREEN CURING AGENT High strength silicone rubber suited for prototyping, production tooling, artistic and renovation applications. Silastic S is recommended for use with polyesters, cement and rigid polyurethanes; als.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Cytec EN-2527 (Conap) Potting and Encapsulation Adhesive Polyurethane Potting and Encapsulating SystemsConathane® EN-2500 series polyurethane potting and encapsulating systems from Cytek have varying degrees of worklife, viscosity and hardness for many s.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | ASTM D638 |
Colorite Polymers 6284 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Dymax 9-20558 Conformal Coating High Performance Light-Curing Adhesives and Coatings for Electronic AssemblyDymax 9-20558 Conformal CoatingThick barrier coating; excellent protection of sensitive circuits from moisture. Cure Speed.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | silicone property; ASTM D412 |
Arlon 25188T010 Silicone Rubber/Laminated ETFE Film Liner: 3 mil PTFE coated fiberglass; Side 1: uncured silicone rubber; Substrate: laminated ETFE film, treated for adhesion |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | silicone property; ASTM D412 |
Arlon 25188T017 Silicone Rubber/Laminated ETFE Film Liner: 3 mil PTFE coated fiberglass; Side 1: uncured silicone rubber; Substrate: laminated ETFE film, treated for adhesion |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | silicone property; ASTM D412 |
Arlon Thermabond® 99180T010 Silicone Rubber/Fiberglass Laminate Low outgassing, thermally conductive, electrically insulating, Thermabond®. Bonds with primer. Liner: 1 mil FEP; Product: uncured silicone rubber; Carrier: 3 mil PTFE coated fiberglass. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | ASTM D412; ISO 37 |
Advanced Polymer Alloys Alcryn® 2250 UT Melt Processable Rubber Alcryn melt-processable rubber (MPR) is a true rubber, based on a partially cross-linked, chlorinated olefin interpolymer alloy. Alcryn is designed for the manufacture of rubber parts with high prod.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | ASTM D412 |
Arlon R3781-920-##R##-P0 Silicone Rubber This fusible silicone tape is specially formulated to yield improved flexibility, elongation and elastic recovery at low operating temperature (-70°C to -100°C) where standard fusible silicone tap.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | TM R050-36 |
Resinlab® EP1200LV Casting Resin Resinlab™ EP1200LV a low viscosity version of EP1200, a highly filled, medium viscosity black casting resin designed for applications requiring a high degree of thermal conductivity, flexibility an.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | TM R050-36 |
Resinlab® SEC1222 Silver Filled Epoxy Adhesive Resinlab™ SEC1222 is a silver filled, two component, room temperature curing epoxy adhesive. It is designed to cure completely at room temperature. SEC1222 provides excellent electrical conductivit.. |
|||
Tensile Strength, Ultimate | 6.89 - 24.1 MPa | 1000 - 3500 psi | Reinforced |
Nitrile Rubber (NBR, Acrylonitrile-Butadiene Rubber) Nitrile Rubbers are copolymers of butadiene and acrylonitrile. The term has also been applied to copolymers of other dienes and/or nitriles. Acrylonitrile content may range from 18-50%. Increasin.. |
|||
Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | |
Loctite® 5145 Form-In-Place Adhesive/Sealant Gasketing and Wire TackersLoctite® innovative gasketing products offer precise, reliable sealing of electronic enclosures, protecting them from environmental hazards. Loctite offers both Form-in-pl.. |
|||
Tensile Strength, Ultimate | 6.89 - 130 MPa | 1000 - 18900 psi | Average value: 80.8 MPa Grade Count:184 |
Overview of materials for Polypropylene with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i.. |