Material Notes:
Information provided by Multibase
Mechanical Properties Metric English Comments
Hardness, Shore A 38
38
post cured- 8 hours at 177°C; ASTM D2240
42
42
molded- without post cure; ASTM D2240
43
43
post cured- 2 hours at 177°C; ASTM D2240
44
44
post cured- 4 hours at 177°C; ASTM D2240
Tensile Strength, Ultimate 6.89 MPa
1000 psi
molded-without post cure; ASTM D412
7.58 MPa
1100 psi
post cured- 2 hours at 177°C; ASTM D412
7.58 MPa
1100 psi
post cured- 4 hours at 177°C; ASTM D412
7.58 MPa
1100 psi
post cured- 8 hours at 177°C; ASTM D412
Tensile Strength, Yield 1.59 MPa
230 psi
at 200%, molded-without post cure; ASTM D412
1.65 MPa
240 psi
200%, post cured- 4 hours at 177°C; ASTM D412
1.65 MPa
240 psi
at 200%, post cured- 2 hours at 177°C; ASTM D412
1.93 MPa
280 psi
200%, post cured- 8 hours at 177°C; ASTM D412
Elongation at Break 740 %
740 %
post cured- 8 hours at 177°C; ASTM D412
770 %
770 %
molded-without post cure; ASTM D412
780 %
780 %
post cured- 2 hours at 177°C; ASTM D412
800 %
800 %
post cured- 4 hours at 177°C; ASTM D412
Tear Strength 26.3 kN/m
150 pli
Die B,molded-without post cure; ASTM D624
28.0 kN/m
160 pli
Die B, post cured- 4 hours at 177°C; ASTM D624
29.8 kN/m
170 pli
Die B, post cured- 8 hours at 177°C; ASTM D624
33.3 kN/m
190 pli
Die B,post cured- 2 hours at 177°C; ASTM D624
Compression Set 50 %
50 %
22 hours at 177°C, molded-without post cure; ASTM D395
52 %
52 %
22 hours at 177°C, post cured- 2 hours at 177°C; ASTM D395
63 %
63 %
22 hours at 177°C, post cured- 4 hours at 177°C; ASTM D395
68 %
68 %
22 hours at 177°C, post cured- 8 hours at 177°C; ASTM D395
Thermal Properties Metric English Comments
Shrinkage 3.20 %

@Temperature 177 °C,
Time 7200 sec
 3.20 %

@Temperature 351 °F,
Time 2.00 hour
 post cured
3.20 %

@Temperature 177 °C,
Time 14400 sec
 3.20 %

@Temperature 351 °F,
Time 4.00 hour
 post cured
3.60 %

@Temperature 177 °C,
Time 28800 sec
 3.60 %

@Temperature 351 °F,
Time 8.00 hour
 post cured