Polymer Property : Tensile Strength, Ultimate = 35000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	241 MPa	35000 psi
Pacific Sintered Materials FN-250-S Nickel Iron Powdered Metal Good impact resistant mechanical components. Good hardenability.Equivalent MPIF Specification: FN-0200-20All information provided by Pacific Sintered Metals.
Tensile Strength, Ultimate	241 MPa	35000 psi	ASTM D638
Quantum Composites Lytex® 9063 63% Glass Fiber Epoxy SMC Lytex 9063 is a high performance, glass fiber reinforced epoxy sheet molding compound designed for military and aerospace structural applications requiring excellent mechanical properties, retention..
Tensile Strength, Ultimate	241 MPa	35000 psi
PSM Industries Pacific Sintered Metals Nickel Iron FN-250-S Powdered Metal Good impact resistant mechanical components, Good hardenability Equivalent MPIF Specification: FN-0200-20Information Provided by Pacific Sintered Metals, a division of PSM Industries
Tensile Strength, Ultimate	241 - 276 MPa	35000 - 40000 psi	Brass butt joint
Lucas-Milhaupt SIL-FOS 5 Silver/ Copper/ Phosphorus Alloy Applications: Sil-Fos 5 was developed primarily for use on copper, but their use has extended to other nonferrous copper base alloys. It is used extensively on refrigeration units, air conditionin..
Tensile Strength, Ultimate	241 - 276 MPa	35000 - 40000 psi	Brass butt joint
Lucas-Milhaupt SIL-FOS Silver/ Copper/ Phosphorus Alloy Applications: Sil-Fos was developed primarily for use on copper, but their use has extended to other nonferrous copper base alloys. It is used extensively on refrigeration units, air conditioning ..
Tensile Strength, Ultimate	241 - 276 MPa	35000 - 40000 psi	Nickel-Silver butt joint
Lucas-Milhaupt SIL-FOS Silver/ Copper/ Phosphorus Alloy Applications: Sil-Fos was developed primarily for use on copper, but their use has extended to other nonferrous copper base alloys. It is used extensively on refrigeration units, air conditioning ..
Tensile Strength, Ultimate	241 - 310 MPa	35000 - 45000 psi	typical
H.C. Starck NRCÂ® 3N5 (UNS R05200) Electron Beam Melted Tantalum Applications: NRCÂ® ETA Tantalum metal products are used where purity and or ductility of the tantalum metal is more important than strength or grain size. Consequently, their primary applicatio..
Tensile Strength, Ultimate	241 - 310 MPa	35000 - 45000 psi	typical
H.C. Starck NRCÂ® 4N (UNS R05200) Electron Beam Melted Tantalum Applications: NRCÂ® ETA Tantalum metal products are used where purity and or ductility of the tantalum metal is more important than strength or grain size. Consequently, their primary applicatio..
Tensile Strength, Ultimate	241 - 310 MPa	35000 - 45000 psi	typical
H.C. Starck NRCÂ® 4N5 (UNS R05200) Electron Beam Melted Tantalum Applications: NRCÂ® ETA Tantalum metal products are used where purity and or ductility of the tantalum metal is more important than strength or grain size. Consequently, their primary applicatio..
Tensile Strength, Ultimate	241 - 310 MPa	35000 - 45000 psi	typical
H.C. Starck NRCÂ® 5N (UNS R05200) Electron Beam Melted Tantalum Applications: NRCÂ® ETA Tantalum metal products are used where purity and or ductility of the tantalum metal is more important than strength or grain size. Consequently, their primary applicatio..
Tensile Strength, Ultimate	241 - 310 MPa @Temperature 20.0 Â°C	35000 - 45000 psi @Temperature 68.0 Â°F	typical
H.C. Starck NRCÂ® Tantalum (UNS R05200) Applications: High strength and excellent corrosion resistance make tantalum ideal for use in the manufacture and repair of chemical process equipment and heat exchangers. Other uses are rupture di..
Tensile Strength, Ultimate	241 MPa @Temperature 871 Â°C	35000 psi @Temperature 1600 Â°F
Haynes HR-160Â® alloy, solution annealed sheet Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Tensile Strength, Ultimate	241 - 372 MPa	35000 - 54000 psi
Eagle Brass 19210 XP-10 Copper Iron, Annealed 19210 has higher strengths than most copper alloys but thanks to its composition and processing it retains formability and conductivity that other copper alloys lose. Typical uses include cooling f..
Tensile Strength, Ultimate	241 MPa	35000 psi	Worked
CMW® D158F Silver Graphite Contact Material For electrical contacts; reduced sticking, low frictionInformation provided by CMW Inc.
Tensile Strength, Ultimate	241 MPa	35000 psi	cold worked
CMW® ELKONIUM 30 pure platinum Platinum has complete freedom from atmospheric corrosion and is preferred for devices that have low closed forces and where surety of making a circuit may be a problem. It has a high melting point (..
Tensile Strength, Ultimate	241 MPa	35000 psi
ATI Allvac® 30, Titanium Alloy, Heat Treatment: 704°C (1300°F) Anneal Data provided by Allvac.Applications: Airframe components, cryogenic vessels, heat exchangers, CPI equipment, condenser tubing, pickling baskets.
Tensile Strength, Ultimate	241 - 310 MPa	35000 - 45000 psi
Bulk Molding Compounds BMC 1401 Encapsulating Material, Electrical Grade BMC 1401 is an electrical grade of encapsulating material characterized by a balance of soft flow and cure rate to ensure complete and proper encapsulation without voiding. Generally too soft for co..