Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 241 - 276 MPa | 35000 - 40000 psi | Brass butt joint |
Lucas-Milhaupt SIL-FOS 5 Silver/ Copper/ Phosphorus Alloy Applications: Sil-Fos 5 was developed primarily for use on copper, but their use has extended to other nonferrous copper base alloys. It is used extensively on refrigeration units, air conditionin.. |
|||
Tensile Strength, Ultimate | 241 - 276 MPa | 35000 - 40000 psi | Brass butt joint |
Lucas-Milhaupt SIL-FOS Silver/ Copper/ Phosphorus Alloy Applications: Sil-Fos was developed primarily for use on copper, but their use has extended to other nonferrous copper base alloys. It is used extensively on refrigeration units, air conditioning .. |
|||
Tensile Strength, Ultimate | 241 - 276 MPa | 35000 - 40000 psi | Nickel-Silver butt joint |
Lucas-Milhaupt SIL-FOS Silver/ Copper/ Phosphorus Alloy Applications: Sil-Fos was developed primarily for use on copper, but their use has extended to other nonferrous copper base alloys. It is used extensively on refrigeration units, air conditioning .. |
|||
Tensile Strength, Ultimate | 255 - 276 MPa | 37000 - 40000 psi | |
Eagle Brass 151 ZHC® COPPER, Annealed Alloy C151 has excellent solderability, high conductivity, and good strength. C151 has superior high temperature softening resistance compared to pure copper C110.Applications can be found in high c.. |
|||
Tensile Strength, Ultimate | 234 - 276 MPa | 34000 - 40000 psi | |
Eagle Brass 210 Gilding Metal, Annealed CDA 210 is known for its resistance to corrosion. The alloy also lends itself to deep drawing such as bullet jackets and electrical applications where formability and conductivity are required. Typi.. |