Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 324 MPa | 47000 psi | ASTM D638 |
Quantum Composites QC-7810 55% Glass Fiber Polyester SMC
(discontinued **) QC-7810 is a toughened thermoset polyester-based sheet molding compound (SMC) designed for compression molding of components requiring high structural strength and flame resistance. It is suggested.. |
|||
Tensile Strength, Ultimate | 324 MPa @Diameter 12.7 mm |
47000 psi @Diameter 0.500 in |
|
Kaiser 6040 T6, T651 Rod & Bar 6040 is a lead-free alternative to 6262. The alloy offers very good machinability along with good corrosion resistance. It also has excellent coating acceptance (anodize response). It can be used in.. |
|||
Tensile Strength, Ultimate | 324 MPa @Diameter 12.7 mm |
47000 psi @Diameter 0.500 in |
|
Kaiser 6040 T8 Rod & Bar 6040 is a lead-free alternative to 6262. The alloy offers very good machinability along with good corrosion resistance. It also has excellent coating acceptance (anodize response). It can be used in.. |
|||
Tensile Strength, Ultimate | 324 - 386 MPa | 47000 - 56000 psi | |
Eagle Brass 110 EPT COPPER, Extra Hard Alloy 110, also known as electrolytic tough pitch (ETP) copper, is commonly used in electric current carrying applications. 110 Copper is 99.9% pure copper with an electrical conductivity rating of .. |
|||
Tensile Strength, Ultimate | 324 - 386 MPa | 47000 - 56000 psi | |
Eagle Brass 151 ZHC® COPPER, 3/4 Hard Alloy C151 has excellent solderability, high conductivity, and good strength. C151 has superior high temperature softening resistance compared to pure copper C110.Applications can be found in high c.. |
|||
Tensile Strength, Ultimate | 324 - 414 MPa | 47000 - 60000 psi | |
Eagle Brass 19210 XP-10 Copper Iron, 1/2 Hard 19210 has higher strengths than most copper alloys but thanks to its composition and processing it retains formability and conductivity that other copper alloys lose. Typical uses include cooling f.. |
|||
Tensile Strength, Ultimate | 324 - 393 MPa | 47000 - 57000 psi | |
Eagle Brass 220 Commercial Bronze, 1/2 Hard CDA 220 is known for having very good corrosion resistance, great cold workability and good hot workability for drawing, blanking, coining, stamping, piercing and punching. Typical uses include plum.. |
|||
Tensile Strength, Ultimate | 324 MPa | 47000 psi | Worked |
CMW® D154F Pre-Oxidized Silver Cadmium Oxide Contact Material ASTM B781 Table 3 For electrical contacts; resistant to welding and high surge currents.Information provided by CMW Inc. |
|||
Tensile Strength, Ultimate | 324 - 386 MPa | 47000 - 56000 psi | |
Eagle Brass 101 OFE COPPER (Certified), Extra Hard Alloy 101 is known as Oxygen-Free Electronic (OFE). It reaches a minimum of 101% IACS conductivity rating. It is the most expensive out of the 101- 110 group because of its higher purity.Information.. |
|||
Tensile Strength, Ultimate | 324 - 386 MPa | 47000 - 56000 psi | |
Eagle Brass 102 OF COPPER (Non-Certified), Extra Hard Alloy 102 is an oxygen-free copper which has better forming, resistance to hydrogen embrittlement, and brazing characteristics than C110 ETP. C102 has good solder-ability and corrosion resistance an.. |
|||
Tensile Strength, Ultimate | 324 MPa | 47000 psi | cold worked |
CMW® ELKONIUM 36 Silver Alloy The alloying of small amounts of one of the precious metals, platinum, palladium or gold with silver increases the hardness, and reduces the metal transfer tendency. These alloys maintain a low cont.. |
|||
Tensile Strength, Ultimate | 324 MPa | 47000 psi | cold worked |
CMW® ELKONIUM 40 pure palladium Palladium belongs to the platinum group of metals and like platinum is highly resistant to atmospheric corrosion; however, it begins to tarnish at temperatures above 400(C. It has a high melting poi.. |
|||
Tensile Strength, Ultimate | 324 MPa | 47000 psi | cold worked |
CMW® ELKONIUM 46 Silver Alloy The alloying of small amounts of one of the precious metals, platinum, palladium or gold with silver increases the hardness, and reduces the metal transfer tendency. These alloys maintain a low cont.. |