Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 379 - 414 MPa | 55000 - 60000 psi | |
Materion BrushCAST® 3C High Conductivity Casting Alloy (As Cast) Pouring Temperature: 1095-1175°CHeat treatment required for max strength (Annealing): 870-900°C/water quenchHeat treatment required for max strength (Hardening): 870-900°C/water quenchDescr.. |
|||
Tensile Strength, Ultimate | 345 - 414 MPa | 50000 - 60000 psi | |
Meehanite Almanite® W1 Wear and Abrasion Resisting Cast Iron Type W1 is an austenitic-martensitic white iron characterized by high hardness and relatively good impact strength. Type W1 has a pearlitic matrix.General Meehanite information - Meehanite metal is.. |
|||
Tensile Strength, Ultimate | 345 - 414 MPa | 50000 - 60000 psi | |
Meehanite Almanite® W2 Wear and Abrasion Resisting Cast Iron Type W2 is an austenitic-martensitic white iron characterized by high hardness and relatively good impact strength. Type W2 has a martensitic matrix.General Meehanite information - Meehanite metal .. |
|||
Tensile Strength, Ultimate | 324 - 414 MPa | 47000 - 60000 psi | |
Eagle Brass 19210 XP-10 Copper Iron, 1/2 Hard 19210 has higher strengths than most copper alloys but thanks to its composition and processing it retains formability and conductivity that other copper alloys lose. Typical uses include cooling f.. |
|||
Tensile Strength, Ultimate | 331 - 414 MPa | 48000 - 60000 psi | |
Eagle Brass 519 Phosphor Bronzes 6%, Annealed Alloy C519 has 6% nominal tin producing higher mechanical strengths with a slight decrease in electrical conductivity when compared to C510 phosphor bronze. Often functionally interchangeable with C.. |