Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 9.30 MPa | 1350 psi | ASTM D638 |
Multibase Multi-Flex® TPE A 8502 CLASSY GREY Heating aging the material 1000 hours at 125°C leads to a +7% change in the tensile strength, +4% change in elongation, and +12% change in tear strength. Ash is 15%. Multi-Flex TPE contains Krato.. |
|||
Tensile Strength, Ultimate | 9.30 MPa | 1350 psi | TPE-0153 (ASTM D 412) |
Advanced Elastomer Systems Trefsin® 3101-85 W305 Thermoplastic Rubber
(discontinued **) A black thermoplastic elastomer with excellent permeation resistance to water, air and other gases. It can be processed using injection molding, extrusion, blow molding or other melt processing tec.. |
|||
Tensile Strength, Ultimate | 9.30 MPa | 1350 psi | TPE-0153 (ASTM D 412) |
Advanced Elastomer Systems Trefsin® 3201-85 W305 Thermoplastic Rubber
(discontinued **) A natural thermoplastic elastomer with excellent permeation resistance to water, air and other gases. It can be processed using injection molding, extrusion, blow molding or other melt processing t.. |
|||
Tensile Strength, Ultimate | 9.30 MPa | 1350 psi | ASTM D638-61T |
Chevron Phillips MarFlex® 1010 LDPE Extrusion Coating Resin
(discontinued **) Resin Type: High Speed ResinCharacteristics: Excellent Processability, High Temperature Extrusion Stability, Good Draw Down ResinApplications: Food Packaging, LaminationsData provided by Chevron Che.. |
|||
Tensile Strength, Ultimate | 9.28 - 138 MPa @Temperature -20.0 - 200 °C |
1350 - 20000 psi @Temperature -4.00 - 392 °F |
Average value: 49.7 MPa Grade Count:1 |
Overview of materials for Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled". Specific grades with glass content between 35% an.. |
|||
Tensile Strength, Ultimate | 9.28 - 138 MPa @Strain 0.230 - 4.21 % |
1350 - 20000 psi @Strain 0.230 - 4.21 % |
Average value: 49.7 MPa Grade Count:1 |
Overview of materials for Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 40% Glass Fiber Filled". Specific grades with glass content between 35% an.. |
|||
Tensile Strength, Ultimate | 9.30 MPa | 1350 psi | |
Kuraray HYBRAR® Low Rebound Compound # 2 Control Description: HYBRAR® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRAR® is a special thermoplastic rubb.. |
|||
Tensile Strength, Ultimate | 9.30 MPa | 1350 psi | ASTM D412 |
Multibase Multi-Flex® TPE A 5401 BLK Ash is 4.71%. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 9.31 MPa | 1350 psi | |
Sylvin Technologies 8950-65 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 9.31 MPa | 1350 psi | |
Sylvin Technologies 9077-80 Natural PVC for Injection Molding Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 9.31 MPa | 1350 psi | |
Sylvin Technologies 9950-65 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 9.32 MPa | 1350 psi | ASTM D412 |
Stellarchem SV-B80E TPV Compound This grade of Stellarchem SV series is a dynamic crosslinked, EPDM/PP compound. It's design to replace thermoset elastomers, such as EPDM, and traditional Thermoplastic TPVs. It can be process on .. |
|||
Tensile Strength, Ultimate | 9.32 MPa | 1350 psi | 500 mm/min; ASTM D 412 |
Zylog Neoplast® 180 C Thermoplastic Vulcanizate Neoplast 180 C is a soft, dynamically vulcanized thermoplastic vulcanizate (TPV), based on polyolefin chemistry, and is intended for Injection Molding and Extrusion applications.RoHS Compliant, UV S.. |
|||
Tensile Strength, Ultimate | 9.31 MPa | 1350 psi | |
Dow Corning SILASTIC® Q7-4735 BIOMEDICAL GRADE ETR ELASTOMER, KIT Two-part, platinum-catalyzed (1:1 by weight), enhanced tear-resistant silicone elastomers are heat cured high consistency silicone rubbers designed for use by customers fabricating medical devices.I.. |
|||
Tensile Strength, Ultimate | 9.30 MPa | 1350 psi | ASTM D638-61T |
Chevron Phillips MarFlex® 1013 LDPE Extrusion Coating Resin Resin Type: High Speed ResinCharacteristics: Excellent Processability, High Temperature Extrusion Stability, Good Draw Down ResinApplications: Food Packaging, LaminationsData provided by Chevron Che.. |
|||
Tensile Strength, Ultimate | 9.30 MPa | 1350 psi | Vulcanizate, Press cured, TC95 +3min at 160°C |
Dow Nordel® IP 4570 Radiator/Heater Hose FormulationNordel® IP 4570 |
|||
Tensile Strength, Ultimate | 9.31 MPa | 1350 psi | ASTM D638 |
Colorite Polymers 5543 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |