Polymer Property : Flexural Yield Strength = 10.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	10.0 - 300 MPa @Temperature -40.0 - 250 °C	1450 - 43500 psi @Temperature -40.0 - 482 °F	Average value: 121 MPa Grade Count:3
Overview of materials for Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled". Specific grades with glass content between 45% an..
Flexural Yield Strength	10.0 - 300 MPa @Thickness 0.790 - 4.00 mm	1450 - 43500 psi @Thickness 0.0311 - 0.157 in	Average value: 121 MPa Grade Count:3
Overview of materials for Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 50% Glass Fiber Filled". Specific grades with glass content between 45% an..
Flexural Yield Strength	10.0 - 207 MPa	1450 - 30000 psi	Average value: 52.0 MPa Grade Count:48
Overview of materials for Polyvinylidinefluoride (PVDF), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyvinylidinefluoride (PVDF), Molded/Extruded". Each property range of values reported is minimum and m..
Flexural Yield Strength	10.0 MPa	1450 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP YP003 Polyester Elastomer (Europe-Africa-Middle East) LNP* LUBRICOMP* YP003 is a compound based on Polyester Elastomer containing PTFE, Silicone. Added features include; Internally Lubricated.