LyondellBasell Hifax™ HSBMF248 Thermoplastic Polyolefin Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin
Manufacturer LyondellBasell
Trade Name Hifax™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Hifax™ HSBMF248 Thermoplastic Polyolefin Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Hifax™ HSBMF248 high melt flow, 1,400 MPa flexural modulus, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent combination of flow, rigidity, low temperature impact resistance and dimensional stability. It was designed for use in thin-walled bumper fascia applications that require high paint durability. Uses: Automotive exterior partsInformation provided by Basell.
Physical Properties Metric English Comments
Density 0.960 g/cc
0.0347 lb/in³
ISO 1183
Melt Flow 17 g/10 min

@Load 2.16 kg,
Temperature 230 °C
17 g/10 min

@Load 4.76 lb,
Temperature 446 °F
Condition L; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 60
60
ISO 868
Tensile Strength at Break 14.0 MPa
2030 psi
ISO 527-1, -2
Tensile Strength, Yield 20.0 MPa
2900 psi
ISO 527-1, -2
Elongation at Break 200 %
200 %
ISO 527-1, -2
Elongation at Yield 5.0 %
5.0 %
ISO 527-1, -2
Flexural Modulus 1.40 GPa
203 ksi
ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature -40.0 °C
1.90 ft-lb/in²

@Temperature -40.0 °F
ISO 180
35.0 kJ/m²

@Temperature -30.0 °C
16.7 ft-lb/in²

@Temperature -22.0 °F
ISO 180
45.0 kJ/m²

@Temperature 23.0 °C
21.4 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Thermal Properties Metric English Comments
CTE, linear 53.0 µm/m-°C

@Temperature -30.0 - 100 °C
29.4 µin/in-°F

@Temperature -22.0 - 212 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 100 °C
212 °F
Unannealed; ISO 75B-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 52.2 °C
126 °F
Unannealed; ISO 75A-1, -2
Shrinkage 0.70 %
0.70 %
Tool, 100x150x3.2 mm; Basell Test Method
0.900 %

@Temperature 121 °C,
Time 3600 sec
0.900 %

@Temperature 250 °F,
Time 1.00 hour
Afterbake, 100x150x3.2 mm; Basell Method