Fujipoly Industries Sarcon® 85GSR Thin-Film GSR

Category Polymer , Thermoset , Silicone
Manufacturer Fujipoly Industries
Trade Name Sarcon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fujipoly Industries Sarcon® 85GSR Thin-Film GSR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sarcon GSR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GSR is a composite of Heat Conductive Silicone Rubber and fiberglass.Information provided by Fujipoly Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 85
85
ASTM D2240
89
89
60°C for 500 hrs with 95% RH; ASTM D2240
90
90
150°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield 17.647 MPa
2559.5 psi
20.0 MPa
2900 psi
150°C for 1,000 hrs; ASTM D1458
20.0 MPa
2900 psi
60°C for 500 hrs with 95% RH
Elongation at Yield <= 3.0 %
<= 3.0 %
<= 3.0 %
<= 3.0 %
150°C for 1,000 hrs; ASTM D1458
<= 3.0 %
<= 3.0 %
60°C for 500 hrs with 95% RH; ASTM D1458
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 182 °C
360 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 3.60e+14 ohm-cm
3.60e+14 ohm-cm
60°C for 500 hrs with 95% RH
1.00e+15 ohm-cm
1.00e+15 ohm-cm
1.20e+16 ohm-cm
1.20e+16 ohm-cm
150°C for 1,000 hrs
Dielectric Constant 3.63

@Frequency 50 Hz
 3.63

@Frequency 50 Hz
 After 1000 hrs at 150°C
3.63

@Frequency 1000 Hz
 3.63

@Frequency 1000 Hz
 After 1000 hrs at 150°C
3.65

@Frequency 1e+6 Hz
 3.65

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
3.66

@Frequency 1e+6 Hz
 3.66

@Frequency 1e+6 Hz
 After 500 hrs at 60°C with 95% RH
3.66

@Frequency 1000 Hz
 3.66

@Frequency 1000 Hz
 After 500 hrs at 60°C with 95% RH
3.68

@Frequency 50 Hz
 3.68

@Frequency 50 Hz
 After 500 hrs at 60°C with 95% RH
3.7

@Frequency 1000 Hz
 3.7

@Frequency 1000 Hz
3.7

@Frequency 1e+6 Hz
 3.7

@Frequency 1e+6 Hz
3.7

@Frequency 50 Hz
 3.7

@Frequency 50 Hz
Dielectric Strength 20.0 kV/mm
508 kV/in
AC 60 Hz
20.0 kV/mm
508 kV/in
AC 60 Hz
22.0 kV/mm
559 kV/in
AC 60 Hz
Dielectric Breakdown 10000 V
10000 V
Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor 0.00040

@Frequency 1e+6 Hz
 0.00040

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
0.00040

@Frequency 1000 Hz
 0.00040

@Frequency 1000 Hz
0.00070

@Frequency 1e+6 Hz
 0.00070

@Frequency 1e+6 Hz
 After 500 hrs at 60°C with 95% RH
0.00070

@Frequency 50 Hz
 0.00070

@Frequency 50 Hz
 After 1000 hrs at 150°C
0.00070

@Frequency 1000 Hz
 0.00070

@Frequency 1000 Hz
 After 1000 hrs at 150°C
0.00090

@Frequency 1e+6 Hz
 0.00090

@Frequency 1e+6 Hz
0.0013

@Frequency 50 Hz
 0.0013

@Frequency 50 Hz
0.0018

@Frequency 1000 Hz
 0.0018

@Frequency 1000 Hz
 After 500 hrs at 60°C with 95% RH
0.0047

@Frequency 50 Hz
 0.0047

@Frequency 50 Hz
 After 500 hrs at 60°C with 95% RH
Descriptive Properties Value Comments
Color White
Thermal Impedance 0.51°C/W
FTM P-3010; ASTM D5470
Thermal Impedance AD Type 0.83°C/W
FTM P-3010; ASTM D5470