SABIC Innovative Plastics NORYL IGN320 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL IGN320 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% glass reinforced PPE + PS. High heat, high modulus automotive applications like ignition coils.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 12.8 g/10 min @Load 5.00 kg, Temperature 300 °C |
12.8 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 6.26 GPa | 908 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 170 MPa | 24700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.72 GPa | 830 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.12 J/cm | 9.59 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C @Thickness 3.20 mm |
327 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C @Thickness 3.20 mm |
316 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 175 °C | 347 °F | Rate B/50; ASTM D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 33.9 kV/mm @Thickness 1.60 mm |
861 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 |
Users viewing this material also viewed the following:
- Nye Lubricants 773A (NG) Synthetic Oil
- Total Lacqrene® 3351(EU) Impact Polystyrene (discontinued **)
- Ineos Nova 2124 High Performance Styrenic Enhanced Polystyrene (discontinued **)
- Sinotek Materials ZSLZ93 Middle Carbon Graphite
- Polyram PlusTek PA325G6 Nylon 6.6, 30% Glass Fiber, Flame Retardant
- Eagle Brass 521 Phosphor Bronzes 8% C, 1/2 Hard
- ExxonMobil Exxsol™ D30 Dearomatized Fluid
- Zeon Chemicals Nipol® NX775 Carboxylated Nitrile Elastomer
- Resinlab® RC8020 Anaerobic Retaining Compound
- M Cubed Technologies ASC-301 Aluminum alloy-30% SiC Metal Matrix Composite
Copyright © lookpolymers.com All Rights Reserved