Borealis Xmod™ GD301HP High Performance 32% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler
Manufacturer Borealis
Trade Name Xmod™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Xmod™ GD301HP High Performance 32% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Xmod GD301HP is reinforced with 32% chemically coupled glass fibers and based on specific Polymer matrix material which is bringing excellent mechanical properties (impact behavior) and very good stiffness even at higher temperatures.Xmod GD301HP has been developed especially for the fluid engineering and automotive market for applications which require high mechanical strengths at high service temperatures. These include pump housings, valves, pedal carriers, and technical components under the bonnet.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow <= 0.0020 cm/cm

@Thickness 2.00 mm
<= 0.0020 in/in

@Thickness 0.0787 in
In Flow Direction; Borealis Method
Linear Mold Shrinkage, Transverse >= 0.010 cm/cm
>= 0.010 in/in
Borealis Method
Melt Flow 4.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
4.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Spiral Flow 95.0 cm

@Thickness 2.00 mm,
Temperature 250 °C
37.4 in

@Thickness 0.0787 in,
Temperature 482 °F
Borealis Method
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 45.0 MPa

@Temperature 100 °C
6530 psi

@Temperature 212 °F
ISO 527-2
Tensile Strength, Yield 108 MPa
15700 psi
At 50 mm/min; ISO 527-2
Elongation at Break 2.9 %
2.9 %
ISO 527-2
7.5 %

@Temperature 100 °C
7.5 %

@Temperature 212 °F
ISO 527-2
Elongation at Yield 3.2 %
3.2 %
Flexural Strain; ISO 178
Tensile Modulus 8.10 GPa
1170 ksi
ISO 527-2
3.50 GPa

@Temperature 100 °C
508 ksi

@Temperature 212 °F
ISO 527-2
Flexural Strength 145 MPa
21000 psi
ISO 178
Flexural Modulus 6.80 GPa
986 ksi
ISO 178
Charpy Impact Unnotched 4.70 J/cm²
22.4 ft-lb/in²
ISO 179/1eU
4.40 J/cm²

@Temperature -20.0 °C
20.9 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched 0.950 J/cm²
4.52 ft-lb/in²
ISO 179/1eA
0.850 J/cm²

@Temperature -20.0 °C
4.05 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
Impact Test 5.00 J

@Temperature -20.0 °C
3.69 ft-lb

@Temperature -4.00 °F
ISO 6603T
6.50 J

@Thickness 3.00 mm
4.79 ft-lb

@Thickness 0.118 in
Biaxial, Total Energy; ISO 6603T
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 152 °C
306 °F
HDT-A; ISO 75-2
Vicat Softening Point 138 °C
280 °F
B (50 N); ISO 306
Shrinkage <= 1.55 %
<= 1.55 %
Testbox; Borealis Method
Processing Properties Metric English Comments
Melt Temperature 220 - 270 °C
428 - 518 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F