Polymer Property : Film Tensile Strength at Break, MD = 36.5 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	36.5 MPa	5300 psi	ASTM D882
ExxonMobil LL 1002.32 Blown Film Resin (discontinued **) LL1002 resins are butene LLDPE designed for blown film process, with good tensile and toughness properties.Information provided by ExxonMobil Chemical
Film Tensile Strength at Break, MD	36.5 MPa	5300 psi	ASTM D882
ExxonMobil LL 1002x74 Blown Film Resin (discontinued **) LL1002 resins are butene LLDPE designed for blown film process, with good tensile and toughness properties.Information provided by ExxonMobil Chemical
Film Tensile Strength at Break, MD	36.5 MPa	5300 psi	ASTM D882
ExxonMobil LL 1002x79 Blown Film Resin (discontinued **) LL1002 resins are butene LLDPE designed for blown film process, with good tensile and toughness properties.Information provided by ExxonMobil Chemical
Film Tensile Strength at Break, MD	36.5 MPa	5290 psi	ASTM D882
DuPont™ Surlyn® 1855 Zinc Ionomer Resin for Blown and Cast Film (discontinued **) Surlyn® 1855 is an ionomer resin available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins. Applications: Meat, poultry, sea..
Film Tensile Strength at Break, MD	36.5 MPa	5300 psi	ASTM D882
LyondellBasell PetrotheneÂ® GA601031 Linear Low Density Polyethylene ApplicationsPETROTHENEÂ® GA 601 series are pelletized, linear low density polyethylenes for applications requiring maximum strength and toughness. These products offer excellent additive homogene..
Film Tensile Strength at Break, MD	36.5 MPa	5300 psi	ASTM D882
LyondellBasell PetrotheneÂ® GA601032 Linear Low Density Polyethylene ApplicationsPETROTHENEÂ® GA 601 series are pelletized, linear low density polyethylenes for applications requiring maximum strength and toughness. These products offer excellent additive homogene..
Film Tensile Strength at Break, MD	36.5 MPa	5300 psi	ASTM D882
LyondellBasell PetrotheneÂ® GA601033 Linear Low Density Polyethylene ApplicationsPETROTHENEÂ® GA 601 series are pelletized, linear low density polyethylenes for applications requiring maximum strength and toughness. These products offer excellent additive homogene..
Film Tensile Strength at Break, MD	36.5 MPa	5300 psi	ASTM D882
LyondellBasell PetrotheneÂ® GA601030 Linear Low Density Polyethylene ApplicationsPETROTHENEÂ® GA 601 series are pelletized, linear low density polyethylenes for applications requiring maximum strength and toughness. These products offer excellent additive homogene..
Film Tensile Strength at Break, MD	36.5 MPa	5300 psi	ASTM D882
ExxonMobil Escorene™ LD 730.09 Blown Ethylene Vinyl Acetate Copolymer Product Description: Escorene Ultra LD 730.09 is a 17.2% vinyl acetate copolymer film resin. LD 730.09 is designed to have superior strength and toughness combined with excellent optics and sealing ..
Film Tensile Strength at Break, MD	36.5 MPa	5290 psi	ASTM D882
DuPont™ Surlyn® 1605 Sodium Ionomer Resin for Blown/Cast Film and Extrusion Coating Surlyn® 1605 is an ionomer resin available for use in conventional blown and cast film extrusion and coextrusion equipment and extrusion coating and coextrusion coating equipment designed to proces..
Film Tensile Strength at Break, MD	36.5 MPa	5300 psi	ASTM D882
ExxonMobil LL 1002.09 Blown Film Resin Product Description: LL 1002 resins are butane LLDPE designed for the blown film process. Films made form LL 1002 resins have very good tensile and toughness properties. LL 1002.09 is a granular mat..
Film Tensile Strength at Break, MD	36.5 MPa	5300 psi	ASTM D882
ExxonMobil LL 1002x75 Blown Film Resin Product Description: LL 1002 resins are butane LLDPE designed for the blown film process. Films made form LL 1002 resins have very good tensile and toughness properties. LL 1002.09 is a granular mat..
Film Tensile Strength at Break, MD	36.5 MPa	5300 psi	ASTM D882
ExxonMobil LLDPE LL 1002.09 Linear Low Density Polyethylene Resin Product Description: LL 1002 resins are butane LLDPE designed for the blown film process. Films made form LL 1002 resins have very good tensile and toughness properties. LL 1002.09 is a granular mat..
Film Tensile Strength at Break, MD	36.5 MPa	5300 psi	ASTM D882
ExxonMobil LLDPE LL 1002.80 Linear Low Density Polyethylene Resin Product Description: LL 1002 resins are butane LLDPE designed for the blown film process. Films made form LL 1002 resins have very good tensile and toughness properties. LL 1002.09 is a granular mat..
Film Tensile Strength at Break, MD	36.5 MPa	5300 psi	ASTM D882
ExxonMobil LLDPE LL 1002X75 Linear Low Density Polyethylene Resin Product Description: LL 1002 resins are butane LLDPE designed for the blown film process. Films made form LL 1002 resins have very good tensile and toughness properties. LL 1002.09 is a granular mat..