ExxonMobil Escorene™ LD 730.09 Blown Ethylene Vinyl Acetate Copolymer

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer	Exxon Chemical
Trade Name	Escorene™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene™ LD 730.09 Blown Ethylene Vinyl Acetate Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: Escorene Ultra LD 730.09 is a 17.2% vinyl acetate copolymer film resin. LD 730.09 is designed to have superior strength and toughness combined with excellent optics and sealing properties.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: No Thermal Stabilizer: YesApplications:Heat Seal LayerPallet Shrink FilmStretch FilmInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.939 g/cc	0.0339 lb/in³	ExxonMobil method
Vinyl Acetate Content	17.2 %	17.2 %	ExxonMobil method
Melt Flow	0.70 g/10 min @Load 2.16 kg, Temperature 190 °C	0.70 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	370 %	370 %	ASTM D882
Film Elongation at Break, TD	660 %	660 %	ASTM D882
Elmendorf Tear Strength MD	50 g	50 g	ASTM D1922
Elmendorf Tear Strength TD	120 g	120 g	ASTM D1922
Dart Drop Test	650 g	1.43 lb	ASTM D1709A
Film Tensile Strength at Break, MD	36.5 MPa	5300 psi	ASTM D882
Film Tensile Strength at Break, TD	36.5 MPa	5300 psi	ASTM D882
1% Secant Modulus, MD	63.4 MPa	9200 psi	ASTM D882
1% Secant Modulus, TD	68.9 MPa	10000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 189 °C	<= 372 °F	Peak Melting Point; ExxonMobil method
Vicat Softening Point	67.2 °C	153 °F	ASTM D1525

Optical Properties	Metric	English	Comments
Haze	1.3 %	1.3 %	ASTM D1003
Gloss	87 %	87 %	45°; ASTM D2457