ExxonMobil LL 1002.09 Blown Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer Exxon Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LL 1002.09 Blown Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LL 1002 resins are butane LLDPE designed for the blown film process. Films made form LL 1002 resins have very good tensile and toughness properties. LL 1002.09 is a granular material which, while it can be used for film production, is also suitable for compounding.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoProcessing Aid: NoThermal Stabilizer: YesApplications: Agricultural FilmBag in BoxBlown FilmCast FilmFood packagingForm Fill and Seal PackagingFreezer FilmGarment FilmGeneral PackagingIndustrial Packaging LinersMulch FilmPackaging FilmsProduce Bags on a Roll Shoppers Trash Can Liners Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ExxonMobil Method
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.48 MPa
1230 psi
ASTM D882
Film Tensile Strength at Yield, TD 8.62 MPa
1250 psi
ASTM D882
Film Elongation at Break, MD 660 %
660 %
ASTM D882
Film Elongation at Break, TD 780 %
780 %
ASTM D882
Puncture Energy 1.11 J
0.817 ft-lb
ExxonMobil
Elmendorf Tear Strength, MD 4.72 g/micron
120 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 13.4 g/micron
340 g/mil
ASTM D1922
Dart Drop 2.76 g/micron
70.0 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 36.5 MPa
5300 psi
ASTM D882
Film Tensile Strength at Break, TD 26.2 MPa
3800 psi
ASTM D882
1% Secant Modulus, MD 177 MPa
25700 psi
ASTM D882
1% Secant Modulus, TD 196 MPa
28400 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 123 °C
253 °F
Peak Melting Temperature; ExxonMobil Method
Optical Properties Metric English Comments
Haze 28.7 %
28.7 %
ASTM D1003
Gloss 22 %
22 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer