Polymer Property : Film Tensile Strength at Break, MD = 21800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	150 MPa	21800 psi	ASTM-D882
Kinlead PL11 Lamination Grade BOPP Plain Film (thickness: 12 Âµm) PL11 is a general, lamination grade BOPP plain film. It is transparent and non heat sealable. It is excellent for extrusion lamination. One side has corona treatment. It is widely used in laminating..
Film Tensile Strength at Break, MD	150 MPa	21800 psi	ASTM-D882
Kinlead PL11 Lamination Grade BOPP Plain Film (thickness: 15 Âµm) PL11 is a general, lamination grade BOPP plain film. It is transparent and non heat sealable. It is excellent for extrusion lamination. One side has corona treatment. It is widely used in laminating..
Film Tensile Strength at Break, MD	150 MPa	21800 psi	ASTM-D882
Kinlead PL21 Lamination Grade BOPP Plain Film (thickness: 12 Âµm) PL21 is a general, lamination grade BOPP plain film. It is transparent and non heat sealable. It is excellent for extrusion lamination. It has excellent dimensional stability, high tensile strength,..
Film Tensile Strength at Break, MD	150 MPa	21800 psi	ASTM-D882
Kinlead PL21 Lamination Grade BOPP Plain Film (thickness: 15 Âµm) PL21 is a general, lamination grade BOPP plain film. It is transparent and non heat sealable. It is excellent for extrusion lamination. It has excellent dimensional stability, high tensile strength,..
Film Tensile Strength at Break, MD	150 - 180 MPa	21800 - 26100 psi	ISO 527-3
Borealis BorPURE™ RB501BF Polypropylene Copolymer BorPure™ RB501BF is a random copolymer. Applications: BorPure™ RB501BF has been developed especially for applications like: food packaging, over wrap film, label film, and shrink film. Additives..
Film Tensile Strength at Break, MD	150 MPa	21800 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 18MB090 OPP Film Product Description: Biaxially oriented polypropylene film metallizable on one side, with a slip controlled broad seal range surface on the other side. Once metalized, film designed to be used in la..
Film Tensile Strength at Break, MD	150 MPa	21800 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 20MB080 OPP Film Product Description: Bicor 20NB080 is a biaxially oriented polypropylene film metallizable on one side, with a heat sealable surface on the other side. Designed to be used after metallization as a s..
Film Tensile Strength at Break, MD	150 MPa	21800 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 29MB080 OPP Film Product Description: A biaxially oriented polypropylene film metallizable on one side, with a heat sealable surface on the other side. Designed to be used after metallization as a single web in HFFS..
Film Tensile Strength at Break, MD	150 MPa	21800 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 29LL210 Preliminary Data Sheet OPP Film Product Description: A biaxially oriented, transparent polypropylene film for pressure sensitive labeling and tape applications.Availability: Africa & Middle East and EuropeKey Features: High yieldG..
Film Tensile Strength at Break, MD	150 MPa	21800 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Metallyte™ 18MM383 OPP Film Product Description: A biaxially oriented very high barrier metalized polypropylene film. This film offers an outstanding moisture barrier and a broad seal range surface on the other side. This film..
Film Tensile Strength at Break, MD	150 MPa	21800 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Metallyte™ 18MM388 OPP Film Product Description: A metallized biaxially oriented polypropylene film, metalized on one side with a broad seal range surface on the other side. This film is designed for high barrier performance p..
Film Tensile Strength at Break, MD	150 MPa	21800 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Metallyte™ 18MM488 OPP Film Product Description: A metalized biaxially oriented polypropylene film, metalized on one side. MM488 is typically used in laminates as the inner web for VFFS and HFFS applications. Due to its slip c..
Film Tensile Strength at Break, MD	150 MPa	21800 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Metallyte™ 18MM883 OPP Film Product Description: An ultra high barrier (UHB), biaxially oriented multilayer polypropylene film. This film has an exceptional barrier to oxygen, flavors and aromas and has an excellent water vapo..
Film Tensile Strength at Break, MD	150 MPa	21800 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Metallyte™ 20MM480 OPP Film Product Description: A metalized biaxially oriented polypropylene film, metalized on one side, heat sealable on the other side. It is typically used in lamination with other substrates on HFFS and V..