ExxonMobil Metallyte™ 18MM883 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Metallyte™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Metallyte™ 18MM883 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: An ultra high barrier (UHB), biaxially oriented multilayer polypropylene film. This film has an exceptional barrier to oxygen, flavors and aromas and has an excellent water vapor barrier. The non-metallized side is treated for adhesive lamination and cold seal applications.Availability: Africa & Middle East, Asia Pacific, Europe, Latin America, North America and South AmericaKey Features:Very high water and gas barrierGood aroma and flavor protectionExcellent metal adhesionEasy convertibility on both sidesExcellent puncture resistanceFeatures:Flavor & Aroma BarrierGas Barrier Light BarrierMoisture BarrierOxygen BarrierTwo Side ProcessableApplications:Biscuits/Cookie/CrackersConfectionery, Chocolate Crisps and SnacksDry Foods and Beverage PowdersHealth and Beauty CareHousehold and DetergentsPet Food Uses: HFFS Flexible Packaging Pouches – Flexible PackagingPre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Middle Web Adhesive Lamination and Outer Web Adhesive LaminationInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 0.0931 g/m²/day @Temperature 38.0 °C |
0.00600 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method |
| Oxygen Transmission Rate | 0.101 cc/m²/day @Temperature 23.0 °C |
0.00650 cc/100 in²/day @Temperature 73.4 °F |
ExxonMobil Method |
| Thickness | 18.0 microns | 0.710 mil | ExxonMobil Method |
| Coating Weight | 16.2 g/m² | 10.1 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 260 MPa | 37700 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 5.0 % @Temperature 135 °C, Time 432 sec |
5.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 5.0 % @Temperature 135 °C, Time 432 sec |
5.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Optical Density | 2.8 | 2.8 | ExxonMobil Method |
| Transmission, Visible | 0.20 % | 0.20 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Yield | 42900 in2/lb |
Users viewing this material also viewed the following:
- Osprey Metals 17-4 PH Stainless Steel Powder (Grade 90% - 22)
- Saint-Gobain Norton® T-200 Mechanical Grade PTFE Sheet (0.062" thick)
- PlastxWorld CEVIAN®-N 050 SAN resin
- Toyobo GLAMIDE® T-808-02 Nylon-6
- Cheng Yu Plastic T888G15 PBT, 15% Glass Fiber
- Elektro-Isola Etronax MF Phenolic, Cotton Fabric Reinforcement, Brown, Sheets
- BASF Polystyrol® 144 C Polystyrene (Europe)
- Beijing Evergrow Resources UHF-F100 UHMW PE Fiber
- Eurostar Star L PA66 15Y D61 PA66, Carbon Filled, Injection Molded
- DuPont™ Sclairfilm® LX-3 LLDPE Film, Laminating, 38.1 µm Thickness (discontinued **)
Copyright © lookpolymers.com All Rights Reserved