Polymer Property : Tensile Strength at Break = 83.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 83.0 MPa
12000 psi
ISO 527
Nilit FRIANYL A63 HH-KV15 Nylon 6.6 for injection molding, 15% glass ball reinforced
Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break 83.0 MPa
12000 psi
ASTM D638
SABIC Innovative Plastics LNP KONDUIT OTF2B PPS - Linear
LNP KONDUIT* OTF2B is a compound based on PPS - Linear resin containing 10% Glass Fiber, 55% Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Tensile Strength at Break 83.0 MPa
12000 psi
5mm/min; ISO 527-2/1A
Celanese Celanex® 7716 PBT, 35% Mineral / Glass Reinforced  (Unverified Data**)
Celanex 7716 is a 35% glass/mineral reinforced, non exuding, flame retarded polybutylene terephthlate which has and excellent balance of mechanical properties and processability. Celanex 7716 is wel..
Tensile Strength at Break 83.0 MPa
12000 psi
ISO 527
Nilit FRIANYL A63 KV15 Nylon 6.6 for injection molding, 15% glass ball reinforced
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break 83.0 MPa
12000 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP EX00548C PEI
LNP LUBRICOMP* EX00548C is a compound based on Polyetherimide resin containing Proprietary Fillers. Added features of this material include: Clean Compounding System, Wear Resistant.
Tensile Strength at Break 83.0 MPa
12000 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP Stat-kon ZEL34XXC PPE+PS (Europe-Africa-Middle East)
LNP* Stat-kon* ZEL34XXC is a compound based on PPE+PS Blend resin containing Carbon Fiber, PTFE. Added features include : Electrically Conductive , Internally Lubricated.This data was supplied by S..
Tensile Strength at Break 83.0 MPa
12000 psi
ISO 527
SABIC Innovative Plastics LNP THERMOCOMP AF006XXZ ABS
LNP* THERMOCOMP* AF006XXZ is a compound based on ABS resin containing 30% Glass Fiber.
Tensile Strength at Break 83.0 MPa
12000 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF002ERH PC
LNP THERMOCOMP* DF002ERH is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding, Healthcare, Mold Release.
Tensile Strength at Break 83.0 MPa
12000 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF002ERJ PC
LNP THERMOCOMP* DF002ERJ is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Healthcare.
Tensile Strength at Break 83.0 MPa
12000 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DX06408 PC
LNP THERMOCOMP* DX06408 is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
Tensile Strength at Break 83.0 MPa
12000 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl GTX GTX4110 PPE+PA66 (Europe-Africa-Middle East)
Non-brominated, non-chorinated Flame Retardant PPE/PA66 alloy, 10% glass reinforced. Combines ductility, modulus and high CTI with dimensional stability.This data was supplied by SABIC-IP for the E..
Tensile Strength at Break 83.0 MPa
12000 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL NH7112 PPE+HIPS
Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to..
Tensile Strength at Break 83.0 MPa
12000 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL NH7112 PPE+HIPS (Asia Pacific)
Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to..
Tensile Strength at Break 83.0 MPa
12000 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL NH7112 PPE+HIPS (Europe-Africa-Middle East)
Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to..
Tensile Strength at Break 83.0 MPa
12000 psi
Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl PKN4717 PPE+PS (Asia Pacific)
PPE+PS. Translucent. FDA compliant. High heat. Foam extrusion. Microwavable. Food packaging uses. Solid properties listed.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break 83.0 MPa
12000 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON AE002 ABS
LNP* STAT-KON* AE002 is a compound based on ABS resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive.
Tensile Strength at Break 83.0 MPa
12000 psi
ISO 527
SABIC Innovative Plastics LNP STAT-LOY PF306 PA 6
LNP* STAT-LOY* PF306 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added feature of this grade includes: Antistat.
Tensile Strength at Break 83.0 MPa
12000 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP 9X02841 PBT+PC
LNP* Thermocmop* 9X02841 is a PBT/Polycarbonate blend containing proprietary fillers.
Tensile Strength at Break 83.0 MPa
12000 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF002ER PC
LNP THERMOCOMP* DF002ER is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding. Mold Release
Tensile Strength at Break 83.0 MPa
12000 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl GTX GTX4110 PPE+PA66
Non-brominated, non-chorinated Flame Retardant PPE/PA66 alloy, 10% glass reinforced. Combines ductility, modulus and high CTI with dimensional stability.This data was supplied by SABIC-IP for the A..
Tensile Strength at Break 83.0 MPa
12000 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl GTX GTX4110 PPE+PA66 (Asia Pacific)
Non-brominated, non-chorinated Flame Retardant PPE/PA66 alloy, 10% glass reinforced. Combines ductility, modulus and high CTI with dimensional stability.This data was supplied by SABIC-IP for the A..
Tensile Strength at Break 83.0 MPa
12000 psi
Longitudinal
Goodfellow Polyaramid/Polyphenylene Sulfide Composite Sheet or Rod
25% Polyaramid fiber - PPS Matrix. Information provided by Goodfellow.
Tensile Strength at Break 83.0 MPa
12000 psi
5 mm/min; ISO 527
CP-Polymer-Technik Wellamid® 6600 GS 30 HWCP 30% Glass Sphere Filled Nylon 66, Heat Stabilized, Dry
Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Strength at Break 83.0 MPa
12000 psi
5 mm/min; ISO 527
Eurostar Staramide BG4ST43 PA6, Glass Fiber Filled, Impact Modified, Injection Molded
Staramide BG4ST43 is an Impact Modified and Glass Fiber Reinforced, Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
Tensile Strength at Break 83.0 MPa
12000 psi
5mm/min; ISO 527-2/1A
Celanese Celanex® 602AC PBT, Glass Reinforced
Celanex 602AC is a 10% fiberglass reinforced PBT that has lower warpage and improved impact over standard PBT.To avoid hydrolytic degradation during processing, CELANEX resins have to be dried to a ..
Tensile Strength at Break 83.0 MPa

@Temperature 120 °C
12000 psi

@Temperature 248 °F
ASTM Test
BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Dry)
Ultramid 8233G HS is a heat stabilized, 33% glass fiber reinforced nylon 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also..
Tensile Strength at Break 83.0 MPa

@Temperature 120 °C
12000 psi

@Temperature 248 °F
ISO Data
BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Dry)
Ultramid 8233G HS is a heat stabilized, 33% glass fiber reinforced nylon 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also..
Tensile Strength at Break 83.0 MPa
12000 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics SABIC PPCOMPOUND G3230A PP
SABIC® PPcompound G3230A is a general purpose, 30% glass filled, chemically coupled, heat stabilized homopolymer polypropylene compound. The IMDS ID is 109612410
Tensile Strength at Break 83.0 MPa
12000 psi
5mm/min; ISO 527-2/1A
Celanese CELANEX 7716 PBT, 35% Mineral / Glass Reinforced
Celanex 7716 is a 35% glass/mineral reinforced, non exuding, flame retarded polybutylene terephthlate which has and excellent balance of mechanical properties and processability. Celanex 7716 is wel..
Tensile Strength at Break 83.0 MPa
12000 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DX06409 PC (Asia Pacific)
LNP* Thermocomp* DX06409 is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.