SABIC Innovative Plastics LNP LUBRICOMP RX85514 PA 66 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP RX85514 PA 66 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* RX85514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ASTM D792
1.27 g/cc
0.0459 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 78.0 MPa
11300 psi
ISO 527
83.0 MPa
12000 psi
ASTM D638
Flexural Modulus 3.57 GPa
518 ksi
ISO 178
3.81 GPa
553 ksi
ASTM D790
Izod Impact, Notched 0.480 J/cm
0.899 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
3.00 kJ/m²

@Temperature -40.0 °C
 1.43 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 158 °C
316 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 140 °C
284 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
131 °C

@Thickness 3.20 mm
 268 °F

@Thickness 0.126 in
 unannealed; ASTM D648