Polymer Property : Tensile Strength at Break = 7980 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 - 55.0 MPa
7250 - 7980 psi
ASTM D638-03
Proto3000 Objet Digital Materials™ DM_7210 Transparent Prototyping Polymer
Primary material: FullCure720Secondary material: TangoBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide ..
Tensile Strength at Break 50.0 - 55.0 MPa
7250 - 7980 psi
ASTM D638-03
Proto3000 Objet Digital Materials™ DM_7220 Transparent Prototyping Polymer
Primary material: FullCure720Secondary material: TangoBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide ..
Tensile Strength at Break 50.0 - 55.0 MPa
7250 - 7980 psi
ASTM D683
Loxim 500 00HB Polycarbonate/Acrylonitrile Butadiene Styrene
Information provided by Loxim Industries
Tensile Strength at Break 50.0 - 55.0 MPa
7250 - 7980 psi
ASTM D683
Loxim 500 00V0 Polycarbonate/Acrylonitrile Butadiene Styrene
Information provided by Loxim Industries
Tensile Strength at Break 41.0 - 55.0 MPa
5950 - 7980 psi
5 mm/min.; IS 867-1963
Amity Thermosets ATG 115 Phenolic Molding Organic Filler, Compression Molded
Characteristics:Medium mechanical strength Medium electrical insulationGeneral purposeColor- Black, BrownSoft/medium flow Applications: Electrical accessories & fittings ( medium quality ) Domestic ..
Tensile Strength at Break 46.0 - 55.0 MPa
6670 - 7980 psi
5 mm/min.; IS 867-1963
Amity Thermosets ATS 1613-R Phenolic Molding Nylon and glass Filler, Compression Molded
Characteristics:High dielectric & mechanical strengthWeather resistant Good electric insulationLow water absorption Good mechanical tension bearing capacityColor-blackMedium flow Applications:Railwa..
Tensile Strength at Break 38.0 - 55.0 MPa
5510 - 7980 psi
ASTM D638
Arkema Group KYNAR® 370 Polyvinylidene Fluoride (PVDF) Homopolymer - Injection Molding
Characteristics: Natural resin - translucent, off-white hemispheres. Low melt shrinkage, graphite powder filled. High stability in harsh thermal, chemical and ultraviolet environments. High toug..
Tensile Strength at Break 34.0 - 55.0 MPa
4930 - 7980 psi
ASTM D638
Arkema Group KYNAR® 710, 710 HDP Polyvinylidene Fluoride Homopolymer- Injection Molding
Characteristics: Natural resin - translucent, off-white hemispheres. HDP indicates higher color stability. High stability in harsh thermal, chemical and ultraviolet environments. High toughness ..
Tensile Strength at Break 34.0 - 55.0 MPa
4930 - 7980 psi
ASTM D638
Arkema Group KYNAR® 740 Black/Red Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion
Characteristics: Pigmented. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeability, abrasion resistance; high purityAppli..
Tensile Strength at Break 34.0 - 55.0 MPa
4930 - 7980 psi
ASTM D638
Arkema Group KYNAR® 740 Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion
Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili..
Tensile Strength at Break 34.0 - 55.0 MPa
4930 - 7980 psi
ASTM D638
Arkema Group KYNAR® 740-02 Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion
Characteristics: Natural resin - translucent, off-white hemispheres. Flame and smoke suppressant. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mecha..
Tensile Strength at Break 34.0 - 55.0 MPa
4930 - 7980 psi
ASTM D638
Arkema Group KYNAR® 760 Polyvinylidene Fluoride Homopolymer - Extrusion
Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili..
Tensile Strength at Break 46.0 - 55.0 MPa
6670 - 7980 psi
5 mm/min.; IS 867-1963
Amity Thermosets ATG 112 Phenolic Molding Organic Filler, Compression Molded
Characteristics:Medium mechanical strength Medium electrical insulationGeneral purposeColor- Black, BrownSoft/medium flow Applications: Electrical accessories & fittings ( medium quality ) Domestic ..
Tensile Strength at Break 46.0 - 55.0 MPa
6670 - 7980 psi
5 mm/min.; IS 867-1963
Amity Thermosets ATR 126 Phenolic Molding Organic Filler, Compression Molded
Characteristics:Ammonia freeGood mouldabilityGood mechanical strengthGood electrical insulationGood surface finishMedium thermal stability Color-black, brownSoft/medium flow Applications:Telecommuni..
Tensile Strength at Break 46.0 - 55.0 MPa
6670 - 7980 psi
5 mm/min.; IS 867-1963
Amity Thermosets ATR 126 Phenolic Molding Organic Filler, Injection Molded
Characteristics:Ammonia freeGood mouldabilityGood mechanical strengthGood electrical insulationGood surface finishMedium thermal stability Color-black, brownSoft flow Applications:Telecommunication ..
Tensile Strength at Break 34.0 - 55.0 MPa
4930 - 7980 psi
ASTM D638
Arkema Group KYNAR® 720, 720 HDP Polyvinylidene Fluoride Homopolymer- Injection Molding and Extrusion
Characteristics: Natural resin - translucent, off-white hemispheres. HDP indicates higher color stability. High stability in harsh thermal, chemical and ultraviolet environments. High toughness ..
Tensile Strength at Break 50.0 - 55.0 MPa
7250 - 7980 psi
ASTM D683
Loxim 830 01 HB Polypropylene Compound, Flame Retardant
Information provided by Loxim Industries
Copyright © lookpolymers.com All Rights Reserved