Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 19.3 MPa | 2800 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable WJJC330 Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | 2 in/min; ASTM D638 |
RheTech Products FT1002-00A Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Step padsHitch padsScuff platesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | 2 in/min; ASTM D638 |
RheTech Products FT4650-01UV Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: Scuff platesExterior grillesBodyside moldingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | 2 in/min; ASTM D638 |
RheTech Products FT4650-581UV Thermoplastic Polyolefin, UV Stabilized, HD2 Medium Quartz Metallic Applications: Scuff platesExterior grillesBodyside moldingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | 2 in/min; ASTM D638 |
RheTech Products FT4702-698UV Thermoplastic Polyolefin, UV Stabilized, RXF Jet Black Applications: Bumper trimExterior componentsDoor claddingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | 2 in/min; ASTM D638 |
RheTech Products FT4702-715UV Thermoplastic Polyolefin, UV Stabilized, ZSP Deep Grey Applications: Exterior componentsGrillesBumper trimDoor componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Elastamax™ HTE 3080 Polyvinyl Chloride + NBR (PVC+NBR) Elastamax™ HTE Series thermoplastic elastomers (TPEs) are based upon compounded blends of PVC resins and nitrile rubber. These elastomeric materials provide outstanding resistance to hydrocarbons a.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible A5DM0 Polyvinyl Chloride, Flexible (PVC, Flexible) Recommended for interior applications.Information provided by PolyOne |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D4894 |
3M Dyneon™ CC503 PTFE, 15% Mineral Filled
(discontinued **) Product Form: White, pelletized free-flowing powder. Applications include bearings - FDA compliant, valve seats, seals.Data provided by Dyneon. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D4894 |
3M Dyneon™ CC622 PTFE 10% Graphite Filled
(discontinued **) Product Form: Black, pelletized free-flowing powder. Applications include bearings, ring seals.Data provided by Dyneon. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D4745 |
3M Dyneon™ CC503 Custom Fluoropolymer Compound
(discontinued **) This compound consists of a mixture of 15% mineral blended with PTFE.Information provided by Dyneon, A 3M Company |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | 510 mm/min; ASTM D412A |
PolyOne Elastamax™ XL 0131-61 Styrene Butadiene Block Copolymer (SBC)
(discontinued **) A thermoplastic elastomer compound formulated for use in food contact applications. The physical properties listed above are typical values obtained on laboratory prepared samples and tested in acco.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D412 |
ITW Devcon Flexane® Rubber Repair / Castable Urethane 94 Liquid, Black Information provided by ITW Devcon |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D1414 |
Greene Tweed FLUORAZ® 797 Fluoroelastomer, FEPM Greene, Tweed`s Fluoraz® functions effortlessly in a variety of challenging process environments. Fluoraz performs well in aggressive chemicals where ultrapure materials are not required. Known f.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D638 |
Teknor Apex APEX® 65004 Polyvinyl Chloride, Flexible Notes: 75°C Jacket; RoHS Compliant Features: Flame Retardant; Sunlight Resistant (720 hours) Uses: Communication Wire JacketingForms: Pellets Agency Ratings: NEC Article 725; NEC Article 760; NEC.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D412 |
Teknor Apex Monprene® MP-2150 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D638 |
Teknor Apex APEX® 65006 Polyvinyl Chloride, Flexible Notes: 75°C Jacket; RoHS Compliant Uses: Wire and Cable ApplicationsForms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D412 |
Teknor Apex Telcar® TL-8431 Thermoplastic Elastomer Notes: RoHS Compliant Uses: Appliance Wire Insulation; Appliance Wire Jacketing; Cable Jacketing; Connectors; Flexible Cord Jacketing; Electrical/Electronic Applications; Industrial Cable Jacketing;.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 1010HF-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 1010HF-01 is an injection molding reactor grade olefinic thermoplastic elastomer (TPO). This product has excellent low temperature impact properties and flow characteristic.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | vs. aluminum; 15 s set time |
Elmer's Products Aron Alpha® 201 Cyanoacrylate Adhesive (Industrial Krazy Glue™) General purpose adhesive for a variety of applications. Various viscosities and gap filling properties available.Low gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | vs. aluminum; 5 s set time |
Elmer's Products Aron Alpha® 202F Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | vs. aluminum; 60 s set time |
Elmer's Products Aron Alpha® 212E Cyanoacrylate Adhesive (Industrial Krazy Glue™) For clean, fast applications. Best for high speed automated assembly.Medium gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on metal substrates. Excellent on porous s.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | vs. aluminum; 5 s set time |
Elmer's Products Aron Alpha® 231F Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | vs. aluminum; 15 s set time |
Elmer's Products Aron Alpha® 241F Cyanoacrylate Adhesive (Industrial Krazy Glue™) Surface insensitive adhesives, ultra-fast setting for porous, soft or tough-to-bond substrates. Series 200TX & Gel: No run, no stringing, excellent gap filling characteristics with good strength on.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D638 |
ExxonMobil LLDPE LL 1001XV Wire & Cable Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 1001 XV is a C4 Ziegler Natta LLDPE for power cable and Telecom jacketing. The grade contains a low level of antioxidants and has excellent Environmental Stress Crack Resista.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | vs. aluminum; 60 s set time |
Elmer's Products Aron Alpha® 252E Cyanoacrylate Adhesive (Industrial Krazy Glue™) For clean, fast applications. Best for high speed automated assembly.High gap fill. Ethyl base monomer. Excellent on rubber/plastic substrates. Fair on metal substrates. Excellent on porous sub.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D638 |
Americas Styrenics EA6740 High Impact Polystyrene Product CharacteristicsVery good printabilityMatte surface finishHigh heat distortion temperatureGood low temperature toughnessFood Contact CompliantTypical ApplicationsPackaging and one-time use it.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D638 |
Americas Styrenics STYRON A-TECH® 1115 High Impact Polystyrene Product CharacteristicsHigh Gloss/High ImpactConsistent colorabilityEasy processingFood Contact CompliantTypical ApplicationsCustom high Gloss Extruded SheetRefrigeration accessoriesSmall Appliances.. |
|||
Tensile Strength at Break | 19.3 MPa | 2800 psi | ASTM D638 ISO 527-2 |
DuPont Elvax® 4355 Ethylene Vinyl Acetate
(discontinued **) DuPont™ Elvax® 4355 is an ethylene-vinyl acetate / acid terpolymer resin for use in industrial applications.ApplicationsElvax® 4355 resins can be used for the following applications: adhesives, s.. |