ExxonMobil LLDPE LL 1001XV Wire & Cable Linear Low Density Polyethylene Resin (European Grade)

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer Exxon Chemical
Trade Name LLDPE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LLDPE LL 1001XV Wire & Cable Linear Low Density Polyethylene Resin (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LL 1001 XV is a C4 Ziegler Natta LLDPE for power cable and Telecom jacketing. The grade contains a low level of antioxidants and has excellent Environmental Stress Crack Resistance (ESCR). Sufficient Carbon Black or UV Stabilizer should be added to meet cable jacketing specifications Availability: Africa & Middle East, Asia Pacific and Europe Additive: Stabilizer: Yes Applications: Halogen-free flame retardant (HFFR) compoundsLV thermoplastic jacketingMV/HV thermoplastic jacketingTelecom thermoplastic jacketingInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.981 g/cc
0.0354 lb/in³
ExxonMobil method
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 49

@Time 15.0 sec
49

@Time 0.00417 hour
ASTM D2240
Tensile Strength at Break 19.3 MPa
2800 psi
ASTM D638
Tensile Strength, Yield 11.7 MPa
1700 psi
ASTM D638
Elongation at Break 830 %
830 %
ASTM D638
Elongation at Yield 20 %
20 %
ASTM D638
Flexural Modulus, 1% Secant 255 MPa
37000 psi
ASTM D790
Thermal Properties Metric English Comments
Melting Point <= 248 °C
<= 478 °F
Peak Melting Point; ExxonMobil method
Electrical Properties Metric English Comments
Volume Resistivity 7.00e+15 ohm-cm
7.00e+15 ohm-cm
ASTM D257
Dielectric Constant 2.2
2.2
ASTM D150
Dielectric Strength 51.2 kV/mm
1300 kV/in
ASTM D149
Dissipation Factor 0.00050
0.00050
ASMT D150