Polymer Property : Tensile Strength at Break = 32000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 221 MPa
32000 psi
ASTM D638
Polymer Resources NY6-G43 Nylon 6, 43% Glass Reinforced
Nylon 6, 43% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are teste..
Tensile Strength at Break 221 MPa
32000 psi
ASTM D638
Ravago Manufacturing Americas Hylon® N1043HL Nylon 6/6 (DAM)
Information provided by Ravago.
Tensile Strength at Break 221 MPa
32000 psi
ASTM D638
Ravago Manufacturing Americas Hylon® N1043L Nylon 6/6 (DAM)
Information provided by Ravago.
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 4008 A (Hot Water Moldable) Polyphthalamide (PPA), Glass Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 4011 A (Hot Water Moldable) Polyphthalamide (PPA), Glass Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 4483 High Temperature Nylon (HTN), Carbon Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D638
Polymer Resources NY6-G43-[color]-H Nylon 6, 43% Glass Reinforced, Heat Stabilized
Nylon 6, 43% Glass Reinforced, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon..
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 2183 Polyetherimide (PEI); Carbon Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 2283 LF Polyetheretherketone (PEEK), Carbon Fiber - Low Flow
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 2299 X 108578 C Polyetheretherketone (PEEK), Long Glass Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 291 Nylon 6/6 (PA), Carbon Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 285 A Nylon 6 (PA); Carbon Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 287 TFE 15 Nylon 6/6 (PA), Carbon Fiber - PTFE Lubricated
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 283 Nylon 6/6 (PA); Carbon Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 4285 Thermoplastic Polyimide (TPI) Carbon Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 4499 X 96265 High Temperature Nylon (HTN), Glass Fiber - PTFE Lubricated - Perfluoropolyether Oil
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 2285 LF TFE 15 Polyetheretherketone (PEEK), Carbon Fiber - PTFE Lubricated
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company RTP 4007 Polyphthalamide (PPA), Glass Fiber
Tensile Strength at Break 221 MPa
32000 psi
ASTM D 638
RTP Company VLF 82311 A Rigid Thermoplastic Polyurethane (RTPU), Long Glass Fiber