- HOME
- POLYMER SEARCH
- Polymer Property : Tensile Strength at Break = 127 MPa
Polymer Property : Tensile Strength at Break = 127 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL38 PC LNP* Lubricomp* DFL-4038 is a Polycarbonate containing 40% Glass Fiber, 15% PTFE. Added features include: Internally Lubricated. |
|||
| Tensile Strength at Break | 127 MPa @Thickness 3.20 mm |
18400 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| LG Chemical Lupox® GP2306FS PBT+GF30% Description: Injection Molding, PBT+GF30%, Flame Retardant, Anti-Hydrolysis Application: IT/OA, E&E (Connector)CAS No. 68928-70-1, 65997-17-3, 24968-12-5 and 1309-64-4Information provided by LG Chem.. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D638 |
| Kotec Carbotex KG-30MRA Polycarbonate, 30% Glass Fiber Reinforced Features: Glass fiber 30% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E .. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp KCL34 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KCL34 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data .. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp PFL34 PA 6 LNP* Lubricomp* PFL34 is a compound based on Nylon 6 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Am.. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp PFL34 PA 6 (Asia Pacific) LNP* Lubricomp* PFL34 is a compound based on Nylon 6 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the As.. |
|||
| Tensile Strength at Break | 127 MPa @Temperature 100 °C |
18400 psi @Temperature 212 °F |
ISO 527-2 |
| Solvay Specialty Polymers Amodel® AS-1566 HS Polyphthalamide (PPA), 65% GlassMineral (Dry) Amodel® AS-1566 HS resin is a 65% glass and mineral reinforced polyphthalamide (PPA) resin that exhibits a high deflection temperature and high flexural modulus. This grade was designed specifica.. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Valox® 414 PBT (Asia Pacific) 40% GR, increased strength/stiffness vs unreinforced. Non-flame retardant. For appliance handles, spotlights, electric motors, pump housings etc.This data was supplied by SABIC-IP for the Asia Pacif.. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON OEL32 PPS - Linear LNP* STAT-KON* OCL32 is a compound based on PPS - Linear resin containing 10% Carbon Fiber, 15% PTFE. Added features of this grade include: Electrically Conductive, Wear Resistant. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON OEP32 PPS - Linear (Asia Pacific) LNP* STAT-KON* OEP32 is a compound based on PPS - Linear resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Electrically Conductive. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-KON RE004MPC PA 66 LNP* STAT-KON* RE004MPC is a compound based on Nylon 66 resin containing 20% Milled Carbon Fiber. Added features of this material are: Exceptional Processing, Clean Compound System, Electrically C.. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® VB-5300GS PBT, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® VB-5302GR PBT, 30% Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP Noryl_HM4025 PPE+PS LNP* Thermocomp* Noryl_HM4025 compound is a 40% Glass/Mineral filled high modulus grade. DTUL 255F (124C). UL94 V-0/V-1/5VA rated in black and gray only (see thicknesses). |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® GP-5300G PBT, Glass Filled Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Thermocomp RFB33 PA6.6 (Europe-Africa-Middle East) LNP*THERMOCOMP* RFB33 is a compound based on PA66 resin containing Glass Bead, Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ISO 527 |
| SABIC Innovative Plastics LNP VERTON MV008S PP LNP VERTON* MV008S is a compound based on Polypropylene resin containing 40% Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, Structural. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ISO 527 |
| SABIC Innovative Plastics LNP VERTON MV008S PP (Europe-Africa-Middle East) LNP VERTON* MV008S is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled, Heat Stabilized. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ISO 527 |
| SABIC Innovative Plastics LNP VERTON MV008SU PP (Asia Pacific) LNP VERTON* MV008SU is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ISO 527 |
| SABIC Innovative Plastics LNP VERTON MV008SU PP (Europe-Africa-Middle East) LNP VERTON* MV008SU is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled, Heat Stabilized, UV-Stabilized. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON OEP32 PPS - Linear LNP STAT-KON* OEP32 is a compound based on PPS - Linear resin containing 10% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Electrically Conductive, Wear Resistant. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOTUF VF008 Super Tough Nylon LNP THERMOTUF* VF008 is a compound based on Super Tough Nylon resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D638 |
| UBE UBESTA® 3020GX6 Glass Fiber Reinforced Nylon 12 Description: UBE UBESTA® Automotive grade Nylon 12Comments: conductive, glass fiber reinforced, UV resistanceInformation provided by UBE. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ISO 527-1 |
| Vyncolit Vyntec® CF8050 Carbon Fiber Reinforced Phenolic VYNTEC CF8030 is a carbon fiber reinforced phenolic moldable composite with excellent tribological properties. It has high mechanical strength combined with low density.Information provided by Sumit.. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D638 |
| A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D638 |
| A. Schulman VOLOY™ 414 30% Glass Fiber Reinforced, Flame Retardant PBT Information provided by A. Schulman. |
|||
| Tensile Strength at Break | 127 MPa @Temperature -40.0 °C |
18400 psi @Temperature -40.0 °F |
ISO Data |
| BASF Ultramid® B3ZG3 15% Glass Filled PA6 (Conditioned) Ultramid B3ZG3 is an impact-modified, 15% glass fiber reinforced injection molding PA6 grade. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | Type I, 5 mm/min; ASTM D638 |
| LNP ULTEM® SMU5832 Polyetherimide, 30% CarbonGlassMineral Reinforced
(discontinued **) ESD characteristics for ultra high-heat applications. Will be UC3010.Features: High Heat ResistanceForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Compan.. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP JF006E PES (Europe-Africa-Middle East) LNP* Thermocomp* JF006E is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding. |
|||
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP VERTON MV008SXP PP (Europe-Africa-Middle East) LNP* Verton* MV008SXP is a compound based on Polypropylene resin containing Long Glass. Added features include: Chemically Coupled, Heat Stabilized. |
|||