SABIC Innovative Plastics LNP Lubricomp PFL34 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp PFL34 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* PFL34 is a compound based on Nylon 6 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D 792 |
| 1.40 g/cc | 0.0506 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.89 % @Time 86400 sec |
0.89 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 127 MPa | 18400 psi | ASTM D 638 |
| 138 MPa | 20000 psi | Type I, 5 mm/min; ASTM D 638 | |
| 138 MPa | 20000 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.1 % | 3.1 % | ASTM D 638 |
| 3.2 % | 3.2 % | Type I, 5 mm/min; ASTM D 638 | |
| 3.2 % | 3.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 7.57 GPa | 1100 ksi | 50 mm/min; ASTM D 638 |
| 7.90 GPa | 1150 ksi | 5 mm/min; ASTM D 638 | |
| 8.23 GPa | 1190 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 172 MPa | 24900 psi | ASTM D 790 |
| 209 MPa | 30300 psi | ISO 178 | |
| 213 MPa | 30900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Yield Strength | 214 MPa | 31000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 5.17 GPa | 750 ksi | ASTM D 790 |
| 6.75 GPa | 979 ksi | 2 mm/min; ISO 178 | |
| 7.00 GPa | 1020 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 1.07 J/cm @Temperature 23.0 °C |
2.00 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 1.33 J/cm @Temperature 23.0 °C |
2.49 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Unnotched | 8.67 J/cm @Temperature 23.0 °C |
16.2 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| 9.69 J/cm @Temperature 23.0 °C |
18.2 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 | |
| Impact Test | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 3.10 µm/m-°C @Temperature -30.0 - 30.0 °C |
1.72 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 0.700 µm/m-°C @Temperature -30.0 - 30.0 °C |
0.389 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C @Thickness 3.20 mm |
426 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C @Thickness 3.20 mm |
396 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| 209 °C @Thickness 3.20 mm |
408 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |