Polymer Property : Ball Indentation Hardness = 125 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	125 MPa	18100 psi	ISO 2039-1
Nilit FRIANYL A63 HH-TFGV 1530 Nylon 6.6 for injection molding, 15% PTFE lubricated, 30% glass fiber reinforced Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	125 MPa	18100 psi	ISO 2039-1
Nilit FRIANYL A63 HS-GV25 Nylon 6.6 for injection molding, 25% glass fiber reinforced Nylon 6.6 for injection molding, high impact resistance.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	125 MPa	18100 psi	ISO 2039-1
Nilit FRIANYL B63 CU90 Nylon 6.6 for injection molding, 90% copper filled Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	125 MPa	18100 psi	ISO 2039-1
Nilit FRIANYL B63 S Nylon 6 for injection molding Nylon 6 for injection molding, light impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	125 MPa	18100 psi	ISO 2039-1
Nilit FRIANYL B63 D-S 5 Nylon 6., std. viscosity for injection molding Nylon 6., std. viscosity for injection molding, permanently flexible, dry impact resistant for high quality dowels.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	125 MPa	18100 psi	ISO 2039-1
Nilit FRIANYL B63 ND Nylon 6 Nylon 6, low viscosity, permanently flexible, dry impact resistant (dowels).Information provided by Frisetta Polymer, which merged into Nilit Plastics
Ball Indentation Hardness	125 - 280 MPa	18100 - 40600 psi	Average value: 213 MPa Grade Count:40
Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. ..
Ball Indentation Hardness	125 MPa	18100 psi	HB 961/30; ISO 2039-1
Akro-Plastic Akromid® S31 (3484) PA 6.10 Dry (discontinued **) A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia..
Ball Indentation Hardness	125 MPa	18100 psi	ISO 2039
GEHR Plastics POM-C Acetal Polyoxymethylene can be used in temperatures up to 100Â°C. The high surface strength is only surpassed by a few materials. POM shows good sliding properties and high resistance to wear and tear be..
Ball Indentation Hardness	125 MPa	18100 psi	Hc 30; ISO 2039; partially
Schwartz Technical Plastics LAMIGAMIDÂ® 310 Cast Polyamide 6, Conditioned Application: sheaves, wheels, rollers, mandrell segments, coupling parts, vibrator parts etc.Information provided by Schwartz Technical Plastics GmbH
Ball Indentation Hardness	125 MPa	18100 psi	conditioned; ISO 2039-1
EMS-Grivory Grivory® LV-3 X ESD black PA12-GF30 Grilamid LV-3 X ESD black is an antistatic Polyamide 12 for injection molding with 30% glass fiber reinforcement. Main attributes are: antistatic with resistivity < 106 Ohmgood fuel and zinc chlorid..
Ball Indentation Hardness	125 MPa	18100 psi	dry; ISO 2039-1
EMS-Grivory Grivory® TSZ 1 PA666 Product description: Grilon TSZ 1 is a heat stabilized, normal viscosity, impact modified PA66 + PA6 injection molding grade. Grilon TSZ 1 has the following important properties: Excellent flow beha..
Ball Indentation Hardness	125 MPa	18100 psi	358/30; ISO 2039-1
BASF Ultraform H 4320 Q600 POM Ultraform H4320 Q600 is an extrusion POM high molecular weight grade. This grade enables high extrusion rates with thick-walled product. It also exhibits high thermal stability and a low tendency ..