Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
PolyOne OnFlex™ BIO 5180D-E0014 Thermoplastic Elastomer (TPE) OnFlex™ BIO 5100 series thermoplastic elastomer compounds are glass reinforced thermoplastic polyurethane compounds made from renewable natural sources. These compounds contain at least 20% renewab.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DBP32EI PC LNP* Lubricomp* DBP32EI is a compound based on Polycarbonate resin containing 15% PTFE/Silicone and 10% Glass Bead. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | at 3.5% strain; ISO 178 |
FKuR Kunststoff Bio-Flex® F 6510 Compostable PLA Blend The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | 2mm/min; ASTM D790 |
Kingfa H-12 Modified ABS Features:UL94 HB @ 1.6-3.0mmHigh toughnessHeat resistanceApplications:Automobile exterior trimAutomobile interior trimPower toolsInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
SABIC Innovative Plastics NORYL SE90 PPE+HIPS (Asia Pacific) |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
SABIC Innovative Plastics NORYL SEH80 PPE+HIPS (Asia Pacific) PPE/HIPS unfilled FR-V1 80C UV improved |
|||
Flexural Strength | 64.0 MPa | 9280 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KA000 Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KA000 is a compound based on Acetal Copolymer resin containing Aramid Fiber, Proprietary Lubricant. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP WP004 PBT LNP* LUBRICOMP* WP004 is a compound based on PBT resin containing 20% PTFE/Silicone. Added feature of this grade is: Wear Resistant. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP AX08306 ABS LNP* THERMOCOMP* AX08306 is a compound based on ABS resin containing Proprietary Filler(s). Added feature of this grade is: Platable. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
SABIC Innovative Plastics NORYL PX2790C PPE+HIPS (Asia Pacific) PPE/HIPS unfilled FR-V1, 90C |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP MF002S PP LNP* Thermocomp* MF002S is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
Plenco 5118 Phenolic, Granular, Injection Molded PLENCO 05118 is a mineral and graphite filled phenolic molding compound, formulated for bearing seals. 05118 provides for a low coefficient of friction, abrasion resistance, minimal water absorptio.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
Eastman DuraStar DS2110UVI Polymer, Natural Durastar DS2110UVI polymer, contains an ultraviolet light stabilization package. It is recommended for indoor applications requiring enhanced color stability upon extended exposure to fluorescent li.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
Eastman DuraStar MN621 Polymer, Natural Durastar Polymer MN621 was developed for the medical device industry and contains a mold release It processes easily and requires minimal drying time. It has superior toughness, high clarity and goo.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
Eastman Eastar BR203 Copolyester Eastar BR203 Copolyester contains a mold release additive. It has excellent appearance and is nearly water-clear. Its most outstanding features are its chemical resistance and processing capabilitie.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
Eastman Tritan TX1800 Copolyester Applications:Consumer and durable goodsExtrusion blow moldingInjection stretch blow moldingKey Attributes:Ease of processingExcellent clarityExcellent Hydrolytic stabilityGood chemical resistanceGoo.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
Eastman Tritan TX1801 Copolyester, Natural Applications:Consumer and durable goodsExtrusion blow moldingInjection stretch blow moldingKey Attributes:Ease of processingExcellent clarityExcellent Hydrolytic stabilityGood chemical resistanceGoo.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | 2 mm/min; ISO 178 |
Chi Mei Polylac® PA-726 ABS Electro-plating |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
Denka TE-10 Transparent Resin Polymer (MABS resin) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
Denka TP-803 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
Entec Hypro™ PPC-GF20 Natural Impact Polypropylene, 20% Glass Reinforced Information provided by Entec |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
Eurostar Star L POM D51 POM, Injection Molded Star L POM D51 is a PTFE Lubricated, POM Copolymer Injection Molding ResinInformation provided by Eurostar. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | 15mm/min; ASTM D790 |
Denka MALECCA K-600 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de.. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 400 POM Easy flowing, fast cycling injection molding grade for manufacturing of thin-wall detailsInformation provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 64.0 MPa | 9280 psi | 23°C, 50% RH; ASTM D790 |
Asahi Kasei Xyron® 140V Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® M104N MPPO Resin High flame retardant, Good flowInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Strength | 64.0 MPa | 9280 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® M104 MPPO Resin Flame retardant, Good flowInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Strength | 64.0 MPa | 9280 psi | 23°C, 50% RH; ASTM D790 |
Asahi Kasei Xyron® 220V Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei |
|||
Flexural Strength | 64.0 MPa | 9280 psi | 2 mm/min; ISO 178 |
Sax Polymers SAXAMID 236Q33 Nylon 6.6, Impact Modified SAXAMID 236Q33 is a impact-modified polyamide 6.6 injection-molding-grade with very good flow properties and outstanding toughness. Even at low temperatures this grade offers super-tough properties... |