SABIC Innovative Plastics LNP Lubricomp KZL34 POM

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp KZL34 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* KZL34 is a compound based on Acetal resin containing Milled Glass and PTFE. Characteristic of this grade is Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.60 g/cc
1.60 g/cc
ASTM D 792
Density 1.65 g/cc
0.0596 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.22 %
0.22 %
23°C / 50% RH; ISO 62
0.14 %

@Time 86400 sec
0.14 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.010 - 0.030 cm/cm

@Time 86400 sec
0.010 - 0.030 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
0.010 - 0.030 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 34.0 MPa
4930 psi
5 mm/min; ISO 527
36.0 MPa
5220 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 37.0 MPa
5370 psi
5 mm/min; ISO 527
38.0 MPa
5510 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 7.0 %
7.0 %
5 mm/min; ISO 527
8.0 %
8.0 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 3.5 %
3.5 %
Type I, 5 mm/min; ASTM D 638
3.5 %
3.5 %
5 mm/min; ISO 527
Tensile Modulus 3.22 GPa
467 ksi
1 mm/min; ISO 527
3.35 GPa
486 ksi
5 mm/min; ASTM D 638
Flexural Strength 64.0 MPa
9280 psi
ISO 178
Flexural Yield Strength 72.0 MPa
10400 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.91 GPa
422 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.96 GPa
429 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.400 J/cm

@Temperature 23.0 °C
0.749 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 3.47 J/cm

@Temperature 23.0 °C
6.50 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 3.00 kJ/m²

@Temperature 23.0 °C
1.43 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 19.0 kJ/m²

@Temperature 23.0 °C
9.04 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
4.00 J

@Temperature 23.0 °C
2.95 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Coefficient of Friction, Dynamic 0.43
0.43
ASTM D 3702 Modified
Coefficient of Friction, Static 0.49
0.49
ASTM D 3702 Modified
K (wear) Factor 10.1 x 10-8 mm³/N-M
5.00 x 10-10 in³-min/ft-lb-hr
Ring; ASTM D 3702 Modified
322 x 10-8 mm³/N-M
160 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 87.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
48.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
CTE, linear, Transverse to Flow 91.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
50.6 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
147 °C

@Thickness 3.20 mm
297 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
90.0 °C

@Thickness 3.20 mm
194 °F

@Thickness 0.126 in
unannealed; ASTM D 648