Vyncolit BXE7670 Glass Filled Phenolic Molding Compound

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Glass Filled
Manufacturer Vyncolit N.V., Sumitomo Bakelite
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Vyncolit BXE7670 Glass Filled Phenolic Molding Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Novolac resin based, mainly glass fiber filled. Due to its unique composition, excellent balance between mechanical, thermal and dimensional stability.Information provided by Sumitomo Bak North America, Inc.
Physical Properties Metric English Comments
Bulk Density 0.590 g/cc
0.0213 lb/in³
ISO 60
Density 1.84 g/cc
0.0665 lb/in³
ISO 1183
Water Absorption 0.060 %
0.060 %
ISO 62
Linear Mold Shrinkage 0.0014 cm/cm
0.0014 in/in
ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 101 MPa
14600 psi
ISO 527-1
Elongation at Break 0.68 %
0.68 %
ISO 527-1
Tensile Modulus 19.0 GPa
2760 ksi
ISO 527-1
Flexural Strength 210 MPa
30500 psi
ISO 178
Flexural Modulus 18.0 GPa
2610 ksi
ISO 178
Compressive Strength 293 MPa
42500 psi
ISO 604
Charpy Impact Unnotched 1.39 J/cm²
6.61 ft-lb/in²
ISO 179-1
Charpy Impact, Notched 0.330 J/cm²
1.57 ft-lb/in²
ISO 179-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 14.0 µm/m-°C
7.78 µin/in-°F
TMA
CTE, linear, Transverse to Flow 50.0 µm/m-°C
27.8 µin/in-°F
TMA
Thermal Conductivity 0.450 W/m-K
3.12 BTU-in/hr-ft²-°F
ASTM E1461
Deflection Temperature at 1.8 MPa (264 psi) >= 223 °C
>= 433 °F
ISO 75 Af
Deflection Temperature at 8.0 MPa 171 °C
340 °F
ISO 75 Cf
Flammability, UL94 V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
Shrinkage 0.040 %
0.040 %
Post Shrinkage; ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 4.15e+13 ohm-cm
4.15e+13 ohm-cm
IEC 60093
Surface Resistance 2.69e+13 ohm
2.69e+13 ohm
IEC 60093
Dielectric Strength 18.0 kV/mm
457 kV/in
IEC 60243-1
Comparative Tracking Index 175 V
175 V
IEC 60250
Descriptive Properties Value Comments
Color Black
Molding Method Compression
Injection
Transfer