Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
PolyOne OnForce™ LFT PP-30LGF/001 Natural Polypropylene Homopolymer (PP Homopolymer) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. .. |
|||
Flexural Strength | 160 - 180 MPa | 23200 - 26100 psi | ISO 178 |
Perstorp Compounds Aminel GF Melamine Fiberglass-reinforced melamine material with high dimensional stability, excellent injection properties and high thermal stabilityInformation provided by Perstorp Compounds Inc. |
|||
Flexural Strength | 160 MPa | 23200 psi | |
Lehmann & Voss LUVOCOM® 1105-8356 PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
Flexural Strength | 160 MPa | 23200 psi | |
Lehmann & Voss LUVOCOM® 50-7110 Polycarbonate, with carbon fiber, low-warpage, easy flowing Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Electrically conductive, suitable for continuous discharging o.. |
|||
Flexural Strength | 160 MPa | 23200 psi | |
Manifattura Cattaneo PA 6 G Nylon Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||
Flexural Strength | 160 MPa | 23200 psi | 1.3 mm/min; ASTM D790 |
Lavergne VYTEEN PCGF10BK PC 10% Glass Reinforced Vyteen PCGF10BK is a 10% fiberglass reinforced general purpose Polycarbonate grade.Features: - Good processabilityTypical Applications: - Laptop computer docking - Laser printer gear - Toner car.. |
|||
Flexural Strength | 160 MPa | 23200 psi | |
Lehmann & Voss LUVOCOM® 1301-7767 PPS, linear, with carbon fiber, lubricant modified Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.Strong, stiff parts.Suitable fo.. |
|||
Flexural Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® DR48V PBT (Europe-Africa-Middle East) VALOX DR48V is a 17% glass reinforced, flame retardant injection moulding PBT resin. Applications: lamp sockets, connectors, switches, electrical housings and bases, bobbins, trimmers and electromot.. |
|||
Flexural Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP Noryl_PCN2910 PPE+PS LNP* Thermodcomp* Noryl_PCN2910 compound is a 35% Glass/Mica filled. High modulus and tight tolerance molding for the chassis market. |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOTUF PX95726 PA 6 LNP THERMOTUF* PX95726 is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Flexural Strength | 160 MPa | 23200 psi | ASTM C1161 |
M Cubed Technologies AAC-501 Aluminum alloy-50% Al2O3 Metal Matrix Composite Produced using SiC preforms and a patented pressureless infiltration process. High SiC content - very high stiffness and strength. Can be used to make very large, complex shapes. Tight as-formed to.. |
|||
Flexural Strength | 160 MPa | 23200 psi | 3.1% strain; ISO 178 |
Borealis Nepol™ GB601HP Polypropylene, 30% Long Glass Fiber Reinforced w/BJ356MO Nepol™ GB601HP is a special long glass fiber reinforced polypropylene concentrate grade intended for injection molding and extrusion. This material is designed for the dilution process in combinat.. |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
Polyram PlusTek PA351M8 Nylon 6.6 for Injection Molding, 40% Mineral Reinforced 40% Minerals Reinforced Nylon 6.6 for injection molding applications.Information provided by Polyram. |
|||
Flexural Strength | 160 MPa | 23200 psi | At Rupture; ISO 178 |
Vyncolit X689 Novolac Phenolic Glass fiber filled and molybdeendisulfide modified phenolic molding compound with excellent mechanical and thermal properties and lower thermal expansion coefficient. It has excellent friction prop.. |
|||
Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
Polyram RamSter PE300J6 PET, 30% Glass Fiber and Glass Bead Reinforced 30% Glass-fiber and glass beads reinforced, high stiffness PET for injection molding applications.Information provided by Polyram Ram On Ind. |
|||
Flexural Strength | 160 MPa @Thickness >=1.50 mm |
23200 psi @Thickness >=0.0591 in |
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1 |
Elektro-Isola Etronit II Phenolic, Paper Reinforcement, Dark Brown, Sheets Description: Mechanical and electrical applications used at normal air humidity. Very good electrical values.Information provided by Elektro-Isola |
|||
Flexural Strength | 160 MPa | 23200 psi | cond; ISO 178 |
DSM EcoPaXX® Q-X07208 PA410-I-GF30 % Glass Reinforced, Impact Modified |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
DuPont Performance Polymers Crastin® LW9020 BK580 PBT+ASA
(Unverified Data**) 20% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9020 BK580 is a 20% glass fiber reinforced black polybutylene terephthalate blend for injection mol.. |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
DuPont Performance Polymers Crastin® LW9030FR BK851 PBT+ASA
(Unverified Data**) 30% Glass Reinforced Flame Retardant Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9030FR BK851 is a 30% glass fiber reinforced flame retardant black polybutylene tere.. |
|||
Flexural Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
Eurostar Starflam PZ0042E PA6, 20% Glass Filled, Injection Molded PZ0042E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding (also known as PF1004Z222 or PA620GFU9Z22)Information provided by Polymer Technol.. |
|||
Flexural Strength | <= 160 MPa | <= 23200 psi | dry, 3.5% flexure; ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 GF15 I Polyamide 6 - Glass Fiber Reinforced 15% Glass fiber reinforced, impact modified, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following mai.. |
|||
Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
Beijing Ranger Chem PBT-201-G15 272 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
Flexural Strength | 160 MPa | 23200 psi | 2mm/min; ISO 178 |
Teijin Panlite® BS-8110R Friction and Abrasion Resistant, Carbon Fiber Reinforced Polycarbonate Resin CF 10% reinforced grade, meeting UL 94 V-2. it is compounded with fluorine powder to improve friction and abrasion resistance and also exhibits a mold release property, maintaining excellent charact.. |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
DuPont Performance Polymers Sorona® FG3015G NC010 Polytrimethylene Terephthalate (PTT)
(Unverified Data** 15% Glass Reinforced Renewably Sourced Polytrimethylene Terephthalate Developed for Food Contact Applications Sorona FG3015G NC010 is a 15% glass fiber reinforced polytrimethylene terephthalate resi.. |
|||
Flexural Strength | 160 MPa | 23200 psi | ISO 178 |
Mitsubishi Xantar® G8F 23 R Polycarbonate-40% Glass Reinforced Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances wher.. |
|||
Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
SABIC Innovative Plastics Lexan® LC108 PC (Asia Pacific) Polycarbonate base, 8% carbon fiber reinforced, FR |