SABIC Innovative Plastics Lexan® LC108 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® LC108 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate base, 8% carbon fiber reinforced, FR
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Water Absorption | 0.13 % @Time 86400 sec |
0.13 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 88 | 88 | ASTM D785 |
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
| Elongation at Break | 4.0 - 6.0 % | 4.0 - 6.0 % | SABIC - Japan Method |
| Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
| Flexural Modulus | 5.98 GPa | 867 ksi | ASTM D790 |
| Izod Impact, Notched | 0.880 J/cm | 1.65 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 35.0 - 59.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
19.4 - 32.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+8 - 1.00e+12 ohm | 1.00e+8 - 1.00e+12 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Plansee S-WVMW Aluminum-potassium Silicate-doped tungsten
- Solvay Specialty Polymers Amodel® ET-1001 L Polyphthalamide (PPA) Resin, Dry as Molded (discontinued **)
- Dow Questra® WA205 High Heat Syndiotactic Polystyrene, 30% Glass Filled (discontinued **)
- Fine Organics FINALUX G 200 Lubricant Additive
- SABIC Innovative Plastics Noryl V0150BT PPE+HIPS (Europe-Africa-Middle East)
- Saint-Gobain Norton® T-200 Mechanical Grade PTFE Sheet (0.250" thick)
- Solvay TECHNYL® A 208F PA66, Conditioned
- Saint-Gobain Vendflow® E-70-V-CE Taste Barrier Tubing Formulation
- PolyOne Synprene® IT 37-034 Thermoplastic Elastomer - SBC, Mineral Filled (discontinued **)
- HP Alloys HPA COBALT Alloy 6B, Wear Resistant, (Co-Cr-W) (UNS R30016)
Copyright © lookpolymers.com All Rights Reserved