Polymer Property : Flexural Strength = 160 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 160 MPa
23200 psi
Plastcom SLOVAMID 6 GF 30 FRA 5 PA6, 30% glass fibre, flame retardant
FeaturesPA 6 for injection moulding, chemically reinforced with 30% glass fibre, with halogen flame retardant. Main features: flammability in accordance with UL 94 V0 at 1.6 mm, glow wire at 960°C,..
Flexural Strength <= 160 MPa
<= 23200 psi
ISO 178
Polykemi AB SCANMID 6 B43^ D F15 Nylon 6, Glass Fiber Reinforced, Modified
Information provided by Polykemi AB
Flexural Strength 160 MPa
23200 psi
2.6 mm/min; ASTM D790
PTS PPE-LXS 314-30 PPE-HIPS, 30% Glass Filled
Typical Applications: Water industrial partsInformation provided by PTS LLC.
Flexural Strength 160 MPa
23200 psi
ISO 178
LookPolymers® 2302 GV1/15 PBT, 15% Glass Reinforced  (Unverified Data**)
Chemical abbreviation according to ISO 1043-1: PBT15% glass fiber reinforced, high glossInformation provided by Celanese
Flexural Strength 160 MPa

@Temperature 23.0 °C
23200 psi

@Temperature 73.4 °F
ISO 178
FG30GT BK010 PCT  (discontinued **)
Thermx® FG30GT BK010 is a 30% glass fiber reinforced, toughened modified polycyclohexylenedimethylene terephthalate resin suitable for repeated-use food-contact US FDA housewares applications.Celen..
Flexural Strength 160 MPa
23200 psi
ASTM D790
Ravago Manufacturing Americas Enviramid™ N1315HL BK Post Consumer Recycle Nylon 66, 15% Glass Filled
Heat Stabilized, Lubricated, Black, and made from EnViramid™ Post Consumer Recycled NylonInformation provided by Ravago.
Flexural Strength 160 MPa
23200 psi
Lehmann & Voss LUVOCOM® 1105-8264 PEEK, with CNT
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Electrically conductive, suitable for continuous discharging of statically generated elect..
Flexural Strength 160 MPa
23200 psi
Lehmann & Voss LUVOCOM® 1700-7910 PPO, with carbon fiber
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; low thermal coefficient of expansion.Electrically conductive, suitable for..
Flexural Strength 160 MPa
23200 psi
Lehmann & Voss LUVOCOM® 1-8181 Polyamide 66, with carbon fiber, toughness-modified
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; impact resistance.Reduced moment of inertia compared with metal parts.Elec..
Flexural Strength 160 MPa
23200 psi
Lehmann & Voss LUVOCOM® 1105-7023/GY PEEK, with glass fiber
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Chemical and hydrolysis resistance parts, non flammable.High dimension..
Flexural Strength 160 MPa
23200 psi
Lehmann & Voss LUVOCOM® 1301-7767 PPS, linear, with carbon fiber, lubricant modified
Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.Strong, stiff parts.Suitable fo..
Flexural Strength 160 MPa
23200 psi
Lehmann & Voss LUVOCOM® 1100-8166 Polyether sulfone, with glass fiber, easy flowing
Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally sta..
Flexural Strength 160 MPa
23200 psi
ISO 178
SABIC Innovative Plastics LNP STAT-KON DEP42E PC
LNP STAT-KON* DEP42E is a compound based on Polycarbonate resin containing 10% Carbon Fiber, 20% PTFE/Silicone. Added features of this material include: Easy Molding. Electrically Conductive, Wear..
Flexural Strength 160 MPa
23200 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Valox® DR48V PBT (Europe-Africa-Middle East)
VALOX DR48V is a 17% glass reinforced, flame retardant injection moulding PBT resin. Applications: lamp sockets, connectors, switches, electrical housings and bases, bobbins, trimmers and electromot..
Flexural Strength 160 MPa
23200 psi
ISO 178
SABIC Innovative Plastics LNP STAT-KON KE004 Acetal Copoly
LNP* STAT-KON* KE004 is a compound based on Acetal Copolymer resin containing 20% Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength 160 MPa
23200 psi
2 mm/min; ISO 178
SABIC Innovative Plastics Valox® IQNH4550 PBT (Europe-Africa-Middle East)
Valox* iQNH4550 resin is a non-brominated/non-chlorinated flame retardant product based on an environmentally sustainable Valox iQ* PBT resin. Post-consumer recycle (PCR) usage is 31% based on EPEAT..
Flexural Strength 160 MPa
23200 psi
ASTM D790
Polyram RamSter PE300J6 PET, 30% Glass Fiber and Glass Bead Reinforced
30% Glass-fiber and glass beads reinforced, high stiffness PET for injection molding applications.Information provided by Polyram Ram On Ind.
Flexural Strength <= 160 MPa
<= 23200 psi
dry, 3.5% flexure; ISO 178
Azoty Tarnow™ Tarnamid® T-27 GF15 I Polyamide 6 - Glass Fiber Reinforced
15% Glass fiber reinforced, impact modified, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following mai..
Flexural Strength 160 MPa
23200 psi
ISO 178
3201 PBT, 15% Glass Reinforced
Celanex 3201 is a 15% glass reinforced general purpose thermoplastic polyester resin that offers a superior combination of mechanical, electrical, and thermal properties, together with outstanding p..
Flexural Strength 160 MPa
23200 psi
ASTM D790
Beijing Ranger Chem PBT-201-G15 272 Flame Retarding FR PBT
Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin..
Flexural Strength 160 MPa
23200 psi
ASTM D790
Beijing Ranger Chem PBT-201-G15 291 Flame Retarding FR PBT
Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin..
Flexural Strength 160 MPa
23200 psi
2mm/min; ISO 178
Teijin Panlite® BS-8110R Friction and Abrasion Resistant, Carbon Fiber Reinforced Polycarbonate Resin
CF 10% reinforced grade, meeting UL 94 V-2. it is compounded with fluorine powder to improve friction and abrasion resistance and also exhibits a mold release property, maintaining excellent charact..
Flexural Strength 160 MPa
23200 psi
Plastcom SLOVALEN PH 49 GF 60 PP reinforced with 60% glass fibre
Features: Modified homopolymer PP for injection moulding, chemically reinforced with 60% glass fibre, contains the modifier of mechanical properties.Very good strength and tensile modulus. Delivered..
Flexural Strength 160 MPa
23200 psi
ISO 178
BASF Ultramid® B3WG6 GP BK 23210 30% Glass Filled PA6 (Conditioned)
Description: 30% Glass fiber reinforced and heat aging resistant injection molding grade used e.g. for automobile manifold.Information provided by BASF
Flexural Strength 160 MPa
23200 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Valox® VX4920 PBT (Europe-Africa-Middle East)
VALOX VX4920 is a 20% glass reinforced nucleated PBT/ASA blend with excellent mechanical properties, high dimensional stability and low density. Applications: connectors and automotive industry.
Flexural Strength 160 MPa
23200 psi
ASTM D570
Solvay Specialty Polymers Xydar® MG-350 Liquid Crystal Polymer, Mineral and Glass Filled  (discontinued **)<
XYDAR MG-350 Liquid Crystal Polymer (LCP) is a mineral and glass-filled injection molding grade developed specifically for cost-effective performance in applications where a balance of flatness and ..
Flexural Strength 160 MPa
23200 psi
Lehmann & Voss LUVOCOM® 1105-7251 PEEK, with glass fiber
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.High dimensionally stable precision parts, high continuous use tempera..
Flexural Strength 160 MPa
23200 psi
ISO 178
Mitsubishi Xantar® G8F 23 R Polycarbonate-40% Glass Reinforced
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances wher..
Flexural Strength 160 MPa
23200 psi
ASTM D790
Gromax CCP PBT 5630-200C 30% Glass Fiber Filled
Product Description: A glass fiber 30% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature Excellent ..
Flexural Strength 160 MPa
23200 psi
ISO 178
Solvay Specialty Polymers Amodel® A-1422 LS WH 171 Polyphthalamide (PPA)  (discontinued **)
Amodel A-1422 LS is a light-stabilized, high-reflectivity, 22%-reinforced white polyphthalamide (PPA) that exhibits high heat resistance, high strength and stiffness over a broad temperature range, ..