DuPont Performance Polymers Sorona® FG3015G NC010 Polytrimethylene Terephthalate (PTT) (Unverified Data**

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyester, TP , Polytrimethylene Terephthalate (PTT)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Sorona® FG3015G NC010 Polytrimethylene Terephthalate (PTT) (Unverified Data**.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Sorona® FG3015G NC010 is a 15% glass fiber reinforced polytrimethylene terephthalate resin containing 31% renewably sourced ingredients by weight (37% based on polymer only) formulated to be food contact compliant.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.44 g/cc	0.0520 lb/in³	ISO 1183
Filler Content	15 %	15 %
Linear Mold Shrinkage, Flow	0.0030 cm/cm @Thickness 2.00 mm	0.0030 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.0070 cm/cm @Thickness 2.00 mm	0.0070 in/in @Thickness 0.0787 in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	120 MPa @Temperature 23.0 °C	17400 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	2.5 % @Temperature 23.0 °C	2.5 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	6.50 GPa @Temperature 23.0 °C	943 ksi @Temperature 73.4 °F	ISO 527
Flexural Strength	160 MPa @Temperature 23.0 °C	23200 psi @Temperature 73.4 °F	ISO 178
Flexural Modulus	5.80 GPa @Temperature 23.0 °C	841 ksi @Temperature 73.4 °F	ISO 178
Izod Impact, Notched (ISO)	5.50 kJ/m² @Temperature 23.0 °C	2.62 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact Unnotched	2.50 J/cm² @Temperature 23.0 °C	11.9 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.550 J/cm² @Temperature 23.0 °C	2.62 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	227 °C	441 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	223 °C	433 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	200 °C	392 °F	ISO 75-1/-2

Processing Properties	Metric	English	Comments
Melt Temperature	260 °C	500 °F	Optimum
	250 - 270 °C	482 - 518 °F
Mold Temperature	80.0 - 110 °C	176 - 230 °F
	100 °C	212 °F	optimum
Drying Temperature	120 °C	248 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	<= 0.020 %	<= 0.020 %

Descriptive Properties	Value	Comments
Appearance	Natural Color
Filler	Glass Reinforced
Forms	Pellets
Generic	Polytrimethylene Terephthalate (PTT)
Material Status	Preliminary Data
Part Marking Code	>PTT-GF15<	ISO 11469
Processing Method	Injection Molding
Product Category	Food Contact Resins
	Glass Reinforced Resins
	Renewably Sourced Resins
Region Available - Global	Yes
Resin Identification	PTT-GF15	ISO 1043
RoHS Compliance	Contact Manufacturer
Uses	Food Applications, Non-specific