SABIC Innovative Plastics Valox® DR48V PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® DR48V PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
VALOX DR48V is a 17% glass reinforced, flame retardant injection moulding PBT resin. Applications: lamp sockets, connectors, switches, electrical housings and bases, bobbins, trimmers and electromotor housings.
Physical Properties Metric English Comments
Specific Gravity 1.52 g/cc
1.52 g/cc
ASTM D792
Density 1.52 g/cc
0.0549 lb/in³
ISO 1183
Filler Content 17 %
17 %
ASTM D229
Moisture Absorption 0.0700 %
0.0700 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.17 %
0.17 %
ISO 62
Viscosity 175000 cP
175000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0035 - 0.0055 cm/cm
0.0035 - 0.0055 in/in
on Tensile Bar; SABIC Method
0.0030 - 0.0090 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0090 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
on Tensile Bar; SABIC Method
Melt Flow 25 g/10 min

@Load 5.00 kg,
Temperature 250 °C
25 g/10 min

@Load 11.0 lb,
Temperature 482 °F
ASTM D1238
50 g/10 min

@Load 5.00 kg,
Temperature 265 °C
50 g/10 min

@Load 11.0 lb,
Temperature 509 °F
ASTM D1238
Melt Index of Compound 8.0 g/10 min

@Load 2.16 kg,
Temperature 250 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
22 g/10 min

@Load 5.00 kg,
Temperature 250 °C
22 g/10 min

@Load 11.0 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
40 g/10 min

@Load 5.00 kg,
Temperature 265 °C
40 g/10 min

@Load 11.0 lb,
Temperature 509 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ISO 2039-2
Hardness, H358/30 218 MPa
31600 psi
ISO 2039-1
Tensile Strength at Break 105 MPa
15200 psi
Type I, 5 mm/min; ASTM D638
105 MPa
15200 psi
5 mm/min; ISO 527
Tensile Strength, Yield 105 MPa
15200 psi
Type I, 5 mm/min; ASTM D638
105 MPa
15200 psi
5 mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
3.0 %
3.0 %
5 mm/min; ISO 527
4.0 %
4.0 %
Flexural Strain, break, 2 mm/min; ISO 178
Elongation at Yield 3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
3.0 %
3.0 %
5 mm/min; ISO 527
Tensile Modulus 7.00 GPa
1020 ksi
5 mm/min; ASTM D638
7.00 GPa
1020 ksi
1 mm/min; ISO 527
Flexural Strength 160 MPa
23200 psi
1.3 mm/min, 50 mm span; ASTM D790
160 MPa
23200 psi
2 mm/min; ISO 178
Flexural Yield Strength 160 MPa
23200 psi
1.3 mm/min, 50 mm span; ASTM D790
160 MPa
23200 psi
2 mm/min; ISO 178
Flexural Modulus 5.70 GPa
827 ksi
2 mm/min; ISO 178
5.80 GPa
841 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.600 J/cm
1.12 ft-lb/in
ASTM D256
0.600 J/cm

@Temperature 0.000 °C
1.12 ft-lb/in

@Temperature 32.0 °F
ASTM D256
0.600 J/cm

@Temperature -30.0 °C
1.12 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 3.80 J/cm
7.12 ft-lb/in
ASTM D4812
3.60 J/cm

@Temperature -30.0 °C
6.74 ft-lb/in

@Temperature -22.0 °F
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature 0.000 °C
2.86 ft-lb/in²

@Temperature 32.0 °F
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²
16.7 ft-lb/in²
80*10*4; ISO 180/1U
30.0 kJ/m²

@Temperature -30.0 °C
14.3 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
3.50 J/cm²
16.7 ft-lb/in²
ISO 179/2C
2.60 J/cm²

@Temperature -30.0 °C
12.4 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
3.00 J/cm²

@Temperature -30.0 °C
14.3 ft-lb/in²

@Temperature -22.0 °F
ISO 179/2C
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.700 J/cm²
3.33 ft-lb/in²
ISO 179/2C
0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 179/2C
Dart Drop, Total Energy 4.00 J

@Temperature 23.0 °C
2.95 ft-lb

@Temperature 73.4 °F
ASTM D3763
Taber Abrasion, mg/1000 Cycles 16
16
CS-17, 1 kg; SABIC Method
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D257
>= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance 2.00e+14 ohm
2.00e+14 ohm
ROA; IEC 60093
Dielectric Constant 3.3

@Frequency 1.00e+6 Hz
3.3

@Frequency 1.00e+6 Hz
ASTM D150
3.3

@Frequency 1.00e+6 Hz
3.3

@Frequency 1.00e+6 Hz
IEC 60250
3.6

@Frequency 50.0 - 60.0 Hz
3.6

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
432 kV/in

@Thickness 0.126 in
in oil; ASTM D149
17.0 kV/mm

@Thickness 3.20 mm
432 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
19.0 kV/mm

@Thickness 1.00 mm
483 kV/in

@Thickness 0.0394 in
short time; IEC 60243-1
23.0 kV/mm

@Thickness 1.60 mm
584 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
23.0 kV/mm

@Thickness 1.60 mm
584 kV/in

@Thickness 0.0630 in
in oil; ASTM D149
Dissipation Factor 0.0020

@Frequency 50.0 - 60.0 Hz
0.0020

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
IEC 60250
0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
ASTM D150
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index >= 150 V
>= 150 V
IEC 60112
175 V
175 V
IEC 60112