Polymer Property : Flexural Strength = 118 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 118 MPa
17100 psi
ASTM D-790
Plaskolite Optix® CP - 81 General Purpose Acrylic Resin
OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli..
Flexural Strength 118 MPa
17100 psi
ASTM D-790
Plaskolite Optix® CP - 82 General Purpose Acrylic Resin
OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli..
Flexural Strength 118 MPa
17100 psi
ASTM D-790
Plaskolite Optix® CP - 82 UVA General Purpose Acrylic Resin
OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli..
Flexural Strength 118 MPa
17100 psi
ASTM D-790
Plaskolite Optix® CP - 86 General Purpose Acrylic Resin
OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli..
Flexural Strength 118 MPa
17100 psi
ASTM D-790
Plaskolite West Optix® CP - 86 General Purpose Acrylic Resin
Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av..
Flexural Strength 118 MPa
17100 psi
ASTM D790
Nilit Polynil® P240HSLV High Viscosity, Heat Stabilized Nylon 66
Description: Polynil P240 HSLV was developed for injection molding applications, where a combination of heat aging resistance, abrasion resistance and impact strength is needed, such as chain tensio..
Flexural Strength 118 MPa
17100 psi
Quadrant EPP Techtron® HPV PPS + solid lubricant, bearing grade, extruded (ISO Data)
As a reinforced, internally lubricated PPS grade, Techtron HPV PPS demonstrates an excellent combination of properties including wear resistance, load-bearing capabilities and dimensional stability ..
Flexural Strength 118 MPa
17100 psi
ISO 178
SABIC Innovative Plastics LNP COLORCOMP JX91550 PES (Asia Pacific)
LNP COLORCOMP* JX91550 is a compound based on Polyethersulfone resin containing Unfilled Custom Color.
Flexural Strength 118 MPa
17100 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC
LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated.
Flexural Strength 118 MPa
17100 psi
ASTM D790
Kolon KOCETAL® GF702 G/F Reinforced Acetal Resin
Glass fiber reinforced, improved stiffness. Applications: Products for high stiffness, improved fatigue properties. Information provided by API-Kolon.
Flexural Strength 118 MPa
17100 psi
ASTM D790
Kotec Carbotex KG-10MRA Polycarbonate, 10% Glass Fiber Reinforced
Features: Glass fiber 10% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E ..
Flexural Strength 118 MPa
17100 psi
ASTM D790
Kotec Carbotex KGN-10MRA Polycarbonate, Flame Retardant, 10% Glass Fiber Reinforced
Features: Glass fiber 10% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E ..
Flexural Strength 118 MPa
17100 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP LL004C PEEK (Asia Pacific)
LNP* Lubricomp* LL004C is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated, Clean Compounding System.
Flexural Strength 118 MPa
17100 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP LL004E PEEK
LNP* LUBRICOMP* LL004E is a compound based on Polyetheretherketone resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
Flexural Strength 118 MPa
17100 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP LL004E PEEK (Asia Pacific)
LNP* Lubricomp* LL004E is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength 118 MPa
17100 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Infino® GP-3200G PBT/ABS, 20% Glass Filled
PBT/ABS with 20% GF reinforcement that can be used in air-conditioner bladesInformation provided by Samsung Cheil Industries.
Flexural Strength 118 MPa
17100 psi
2.8 mm/min; ASTM D638
Samsung Cheil Industries Infino® VB-8102G MPPE, Glass Filled FR
Information provided by Samsung Cheil Industries.
Flexural Strength 118 MPa
17100 psi
2.8 mm/min; ASTM D638
Samsung Cheil Industries Infino® XK-2307 PPS
Information provided by Samsung Cheil Industries.
Flexural Strength 118 MPa
17100 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Infino® EM-8240C MPPE, Glass Filled
MPPE/GF material that is used in the main frame of banknote sortersInformation provided by Samsung Cheil Industries.
Flexural Strength 118 MPa
17100 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP LL004 PEEK
LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing 20% PTFE. Added feature of this material is: Wear Resistant.
Flexural Strength 118 MPa
17100 psi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP LL004 PEEK (Asia Pacific)
LNP LUBRICOMP* LL004 is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength 118 MPa
17100 psi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS
LNP* THERMOCOMP* ZF0049 is a compound based on PPE+PS resin containing 20% Glass Fiber. Added feature of this material is: Flame Retardant.
Flexural Strength 118 MPa
17100 psi
2.8 mm/min; ASTM D638
Samsung Cheil Industries Infino® VB-8102G MPPE, Glass Filled FR
Information provided by Samsung Cheil Industries.
Flexural Strength 118 MPa
17100 psi
ISO 178
Unitika A3130 PA6, 35% Mineral Reinforced, Dry
Information provided by Unitika Ltd.
Flexural Strength 118 MPa
17100 psi
2 mm/min; ISO 178
Eurostar Starflam AFR560B5 PA66, Mineral/Glass Fiber Reinforced, Flame Retardant, Injection Molding
Starflam AFR560B5 is a Flame Retardant, Mineral Filled and Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Flexural Strength 118 MPa
17100 psi
Dry; ASTM D790
Asahi Kasei Leona® 1502 Nylon 66
Similar to 1500 but with improved heat aging resistance.Applications:Under-the-hood automotive parts Information provided by Asahi Kasei
Flexural Strength 118 MPa
17100 psi
2.8mm/min; ASTM D790
Asia International Enterprise (Hong Kong) 6010FGN Nylon 66
Information provided by Asia International Enterprise (Hong Kong) Ltd.
Flexural Strength 118 MPa
17100 psi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp MF0069S PP
LNP* Thermocomp* MF0069S is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Chemically Coupled, Flame Retardant, Heat Stabi..
Flexural Strength 118 MPa
17100 psi
2.0 in/min; ASTM D790
LTL Color Compounds ColorFast® NY1 Nylon 6
Injection molding nylon 6, with or without lubeAll information provided by LTL Color Compounders, Inc.