SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0065 cm/cm @Time 86400 sec |
0.0065 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 67.0 MPa | 9720 psi | ASTM D638 |
| 67.0 MPa | 9720 psi | ISO 527 | |
| Tensile Strength, Yield | 71.0 MPa | 10300 psi | ASTM D638 |
| 71.0 MPa | 10300 psi | ISO 527 | |
| Elongation at Break | 5.5 % | 5.5 % | ASTM D638 |
| 5.8 % | 5.8 % | ISO 527 | |
| Elongation at Yield | 3.3 % | 3.3 % | ASTM D638 |
| 3.3 % | 3.3 % | ISO 527 | |
| Tensile Modulus | 4.13 GPa | 599 ksi | 50 mm/min; ASTM D638 |
| 4.15 GPa | 602 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
| Flexural Modulus | 3.90 GPa | 566 ksi | ISO 178 |
| 4.13 GPa | 599 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.44 J/cm | 2.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.36 J/cm | 13.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 48.0 kJ/m² | 22.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 23.0 J | 17.0 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.37 | 0.37 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.43 | 0.43 | ASTM D3702 Modified |
| K (wear) Factor | 332 x 10-8 mm³/N-M | 165 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 55.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 56.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 55.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 56.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |