Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
Plaskolite Optix® CA-82 General Purpose Acrylic Resin Injection Molding Grade Pellets. Highest Molecular Weight, good heat resistance. Superior mold release. |
|||
Flexural Strength | 118 MPa | 17100 psi | ASTM D-790 |
Plaskolite Optix® CP - 81 General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli.. |
|||
Flexural Strength | 118 MPa | 17100 psi | ASTM D-790 |
Plaskolite Optix® CP - 82 General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli.. |
|||
Flexural Strength | 118 MPa | 17100 psi | ASTM D-790 |
Plaskolite West Optix® CP - 86 General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av.. |
|||
Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
NOVA Chemicals DYLARK® 480P16 Glass Reinforced Engineering Resin Features:Very high modulus High heat resistance Excellent flow characteristics Excellent adhesion to urethaneApplications:Instrument panel substrates Consoles Cluster housings Interior trimInformati.. |
|||
Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated. |
|||
Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC (Asia Pacific) LNP* Lubricomp* DFL22 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Strength | 118 MPa | 17100 psi | ASTM D-790 |
Plaskolite West Optix® CP - 81 General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av.. |
|||
Flexural Strength | 118 MPa | 17100 psi | ASTM D-790 |
Plaskolite West Optix® CP - 82 UVA General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av.. |
|||
Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
Kolon KOCETAL® GF702 G/F Reinforced Acetal Resin Glass fiber reinforced, improved stiffness. Applications: Products for high stiffness, improved fatigue properties. Information provided by API-Kolon. |
|||
Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
LG Chemical LUCON PO-3000 Electrically Conductive Thermoplastic LG Chemicals has formulated a diverse range of LUCON thermoplastic compounds containing conductive additives, such as carbon powder, (nickel coated) carbon fiber, or stainless steel fiber for solvin.. |
|||
Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
Kotec Carbotex KG-10MRA Polycarbonate, 10% Glass Fiber Reinforced Features: Glass fiber 10% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E .. |
|||
Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
Kotec Carbotex KGN-10MRA Polycarbonate, Flame Retardant, 10% Glass Fiber Reinforced Features: Glass fiber 10% reinforced, Mold release, Translucent, Dimensional stability, Flame retardant, High rigidityApplications: OA equipment, Communications, Precision parts, Machineries, E & E .. |
|||
Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP LL004C PEEK (Asia Pacific) LNP* Lubricomp* LL004C is a compound based on Polyetheretherketone resin containing PTFE. Added features of this material include: Internally Lubricated, Clean Compounding System. |
|||
Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP LL004E PEEK LNP* LUBRICOMP* LL004E is a compound based on Polyetheretherketone resin containing 20% PTFE. Added feature of this material is: Wear Resistant. |
|||
Flexural Strength | 118 MPa | 17100 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® EM-8240C MPPE, Glass Filled MPPE/GF material that is used in the main frame of banknote sortersInformation provided by Samsung Cheil Industries. |
|||
Flexural Strength | 118 MPa | 17100 psi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® VB-8102G MPPE, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 118 MPa | 17100 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® EM-8240C MPPE, Glass Filled MPPE/GF material that is used in the main frame of banknote sortersInformation provided by Samsung Cheil Industries. |
|||
Flexural Strength | 118 MPa | 17100 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® HF-3200H PC, Glass Filled High Impact Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 118 MPa | 17100 psi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® XK-2307 PPS Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 118 MPa | 17100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP ZF004 PPE+PS LNP THERMOCOMP* ZF004 is a compound based on PPE+PS resin containing 20% Glass Fiber. |
|||
Flexural Strength | 118 MPa | 17100 psi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific) LNP* Thermocomp* ZF0049 is a compound based on PPE+PS Blend resin containing Flame Retardant. Added features of this material include: Flame Retardant. |
|||
Flexural Strength | 118 MPa | 17100 psi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® VB-8102G MPPE, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 118 MPa | 17100 psi | Dry; ASTM D790 |
Asahi Kasei Leona® 1300S Nylon 66 General purpose grade. Good balance of flowability and mechanical properties.Applications:Connectors, washers, cable ties. Information provided by Asahi Kasei |
|||
Flexural Strength | 118 MPa | 17100 psi | Dry; ASTM D790 |
Asahi Kasei Leona® 1700S Nylon 66 Similar to 1500 but with even higher molecular weight. Suitable for extrusion of thick-wall parts.Applications:Rods, films Information provided by Asahi Kasei |
|||
Flexural Strength | 118 MPa | 17100 psi | Dry; ASTM D790 |
Asahi Kasei Leona® FR200 Nylon 66 UL94 V-0; halogen-free and phosphor-free.Applications:Connectors, switches, and other electrical and electronic parts Information provided by Asahi Kasei |
|||
Flexural Strength | 118 MPa | 17100 psi | ASTM D-790 |
Plaskolite Optix® CP - 80 General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli.. |
|||
Flexural Strength | 118 MPa | 17100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp MF0069S PP LNP* Thermocomp* MF0069S is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Chemically Coupled, Flame Retardant, Heat Stabi.. |
|||
Flexural Strength | 118 MPa | 17100 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® GP-3200G PBT/ABS, 20% Glass Filled PBT/ABS with 20% GF reinforcement that can be used in air-conditioner bladesInformation provided by Samsung Cheil Industries. |
|||
Flexural Strength | 118 MPa | 17100 psi | 2.0 in/min; ASTM D790 |
LTL Color Compounds ColorFast® NY1 Nylon 6 Injection molding nylon 6, with or without lubeAll information provided by LTL Color Compounders, Inc. |