Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 6.20 - 16.7 GPa | 899 - 2420 ksi | Average value: 11.1 GPa Grade Count:11 |
Overview of materials for Polyaryletherketone (PAEK), Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyaryletherketone (PAEK), Glass Fiber Filled". Each property range of values reported is minimum and m.. |
|||
Modulus of Elasticity | 6.20 - 7.50 GPa @Temperature 60.0 - 120 °C |
899 - 1090 ksi @Temperature 140 - 248 °F |
Average value: 6.90 GPa Grade Count:1 |
Overview of materials for Polycarbonate, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 30% Glass Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Modulus of Elasticity | 6.20 GPa | 899 ksi | ISO 527 |
BASF Ultramid® B3EG6 30% Glass Filled PA6 (Conditioned) Ultramid B3EG6 is a 30% glass fiber reinforced injection molding PA6 grade. It conforms to FDA requirements of 21 CFR 177.1500. |
|||
Modulus of Elasticity | 6.20 GPa | 899 ksi | ISO 527 |
BASF Ultramid® B3EG6 BK00564 30% Glass Filled PA6 (Conditioned) Ultramid B3EG6 BK00564 is a 30% glass fiber reinforced, pigmented black injection molding PA6 grade. It conforms to FDA requirements of 21 CFR 177.1500. |
|||
Modulus of Elasticity | 6.20 GPa | 899 ksi | ISO 527-1/-2 |
BASF Ultramid® S3EG6 Balance 30% Glass Filled PA 610 (Conditioned) Description: BASF supplies polyamide 610 for processing by injection molding under the trade name Ultramid® Balance which is produced by polycondensation of hexamethylene diamine and sebacic acid. .. |
|||
Modulus of Elasticity | 6.20 GPa | 899 ksi | ISO 527-1/-2 |
BASF Ultramid® S3WG6 Balance 30% Glass Filled PA 610 (Conditioned) Description: BASF supplies polyamide 610 for processing by injection molding under the trade name Ultramid® Balance which is produced by polycondensation of hexamethylene diamine and sebacic acid. .. |
|||
Modulus of Elasticity | 6.20 GPa | 899 ksi | ISO 527 |
BASF Ultramid® B3WG6 BK00564 30% Glass Filled PA6 (Conditioned) Ultramid B3WG6 BK00564 is a 30% glass fiber reinforced, pigmented black, heat stabilized injection molding PA6 grade. |
|||
Modulus of Elasticity | 6.20 GPa | 899 ksi | Conditioned; ISO 178 |
Addiplast Addinyl B2 V40 Nylon 6, 40% Glass Filled Glass fiber reinforced, high strengthInformation provided by Addiplast. |
|||
Modulus of Elasticity | 6.20 GPa | 899 ksi | Conditioned; ISO 178 |
Addiplast Addinyl B2 ZV40 Nylon 6, 40% Glass Filled Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast. |