Polymer Property : Modulus of Elasticity = 1900 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	6.90 - 13.1 GPa	1000 - 1900 ksi	Average value: 10.7 GPa Grade Count:5
Overview of materials for Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled". Each property range of values reported i..
Modulus of Elasticity	8.80 - 13.1 GPa	1280 - 1900 ksi	Average value: 10.3 GPa Grade Count:6
Overview of materials for Phenolic, Novolac, Heat Resistant Grade, Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Heat Resistant Grade, Filled". Each property range of values reported is minimum and ..
Modulus of Elasticity	3.70 - 13.1 GPa	537 - 1900 ksi	Average value: 8.03 GPa Grade Count:45
Overview of materials for Nylon 66, Glass/Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass/Mineral Filled". Each property range of values reported is minimum and maximum values of..
Modulus of Elasticity	5.17 - 13.1 GPa	750 - 1900 ksi	Average value: 8.41 GPa Grade Count:10
Overview of materials for Nylon 66, Mineral Filled, NCG Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Mineral Filled, NCG Fiber Filled". Each property range of values reported is minimum and maxim..
Modulus of Elasticity	4.10 - 13.1 GPa	595 - 1900 ksi	Average value: 8.77 GPa Grade Count:19
Overview of materials for Polybutylene Terephthalate (PBT), Glass Fiber + PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Fiber + PTFE Filled". Each property range of values reported is ..