Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 4.10 - 18.7 GPa | 595 - 2710 ksi | Average value: 15.1 GPa Grade Count:26 |
Overview of materials for Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled". Specific grades with glass content between 45.. |
|||
Modulus of Elasticity | 4.10 - 8.64 GPa | 595 - 1250 ksi | Average value: 7.00 GPa Grade Count:5 |
Overview of materials for Phenolic; Unreinforced; Molded This property data is a summary of similar materials in the MatWeb database for the category "Phenolic; Unreinforced; Molded". Each property range of values reported is minimum and maximum values of.. |
|||
Modulus of Elasticity | 4.10 - 20.0 GPa | 595 - 2900 ksi | Average value: 14.3 GPa Grade Count:24 |
Overview of materials for Nylon 12, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. .. |
|||
Modulus of Elasticity | 4.10 GPa | 595 ksi | Sample Type 1B, 50 mm/min; ISO 527-1/2:1993 |
Global EPP PA 6C MOLY Cast Polyamide 6 + MoS2 Cast nylons are generally accepted as the primary engineering polymer, suitable for virtually any plain bearing application. By varying the conditions of polymerisation the mechanical properties of .. |
|||
Modulus of Elasticity | 4.10 GPa | 595 ksi | std. dev. 0.55 GPa |
Schmelzer Industries Pearlveil 110-10 Fiberglass Veil Economical alternative for flat or shallow applications. Suitable for hand lay-up, pre-form molding, press molding, vacuum molding, and injection molding. Data provided by the manufacturer, Schmel.. |
|||
Modulus of Elasticity | 4.10 GPa | 595 ksi | ISO 178 |
Addiplast Addilene J 420 K24 Polypropylene Copolymer High densityInformation provided by Addiplast. |
|||
Modulus of Elasticity | 4.10 - 11.0 GPa | 595 - 1600 ksi | Average value: 8.69 GPa Grade Count:7 |
Overview of materials for Nylon 46, Lubricated + Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Lubricated + Glass Fiber Reinforced". Each property range of values reported is minimum and ma.. |
|||
Modulus of Elasticity | 4.10 - 4.50 GPa @Temperature 60.0 - 150 °C |
595 - 653 ksi @Temperature 140 - 302 °F |
Average value: 4.33 GPa Grade Count:1 |
Overview of materials for Polyethersulfone (PES), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% a.. |
|||
Modulus of Elasticity | 4.10 - 13.1 GPa | 595 - 1900 ksi | Average value: 8.77 GPa Grade Count:19 |
Overview of materials for Polybutylene Terephthalate (PBT), Glass Fiber + PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Fiber + PTFE Filled". Each property range of values reported is .. |