Polymer Property : Compressive Strength = 24000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Strength	165 MPa @Temperature 23.9 °C	24000 psi @Temperature 75.0 °F	Dry; 325°F, 1000psi Cured; ASTM D695
Park Electrochemical Nelcote® F-502 Phenolic Prepreg, Silica Reinforced Nelcote® F-502 is a MIL-R-9299 phenolic resin system suitable for impregnation on any MIL-C-9084 fabric with a compatible finish. F-502 is used in the manufacture of ablative reinforcements in rock..
Compressive Strength	165 MPa @Temperature 23.9 °C	24000 psi @Temperature 75.0 °F	Dry; 325°F Autoclave; ASTM D695
Park Electrochemical Nelcote® F-554 Phenolic Prepreg, Aerospace Silica Fabric Reinforced Nelcote® F-554 is a high purity silica filled phenolic resin coated on Commercial or Aerospace grade silica fabric. F-554 is used in the manufacture of intermediate temperature ablative rocket nozz..
Compressive Strength	165 MPa @Temperature 23.9 °C	24000 psi @Temperature 75.0 °F	Dry; 325°F Autoclave; ASTM D695
Park Electrochemical Nelcote® F-557 Phenolic Prepreg, Commercial Silica Fabric Reinforced Nelcote® F-557 is a high purity silica filler phonic resin coated on Commercial or Aerospace grade silica fabric. F-557 is used in the manufacture of intermediate temperature ablative rocket nozzle..
Compressive Strength	165 MPa @Temperature 23.9 °C	24000 psi @Temperature 75.0 °F	Dry; ASTM D695
Park Electrochemical Nelcote® S-860 Silicone Prepreg, 1581-112NPH E-Glass Reinforced Nelcote® S-860 is a MIL-P-25518 type silicone resin with a good combination of electrical and high temperature properties. GMS4001 qualified specificationsKey Features and Benefits:500°F maximum s..
Compressive Strength	165 MPa	24000 psi	10% Def.; ASTM D695
Quadrant EPP Techtron® PSGF PPS - Compression Molded 40% Glass Reinforced Polyphenylene Sulfide (ASTM Product Data Sheet)
Compressive Strength	165 MPa	24000 psi	10% Def.; ASTM D695
Quadrant EPP Semitron® CMP XL20 (ASTM Product Data Sheet)
Compressive Strength	>= 165 MPa	>= 24000 psi
Master Bond EP46HT-2Med Two Component Heat Resistant Biocompatible Epoxy System Master Bond Polymer System EP46HT-2MED is a two component medical grade epoxy system for high performance structural bonding and casting suitable for applications where resistance to temperatures fr..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced FR Polyester Flat Sheet, 3/16" to 1/4" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced FR Polyester Flat Sheet, 3/8" to 1" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced Polyester Flat Sheet, 3/16" to 1/4" Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded products feature:High StrengthCorrosion Resistant to many che..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced Vinylester Flat Sheet, 1/8" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced Vinylester Flat Sheet, 3/16" to 1/4" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced Vinylester Flat Sheet, 3/8" to 1" Flame retardant grade; see details in the property table.Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded prod..
Compressive Strength	165 MPa	24000 psi	ASTM D695
Applied Composites 8038 Polyester SMC Industry Application: TransportationProduct Application: Mass TransitDistinct Features: Low Smoke Construction and Mass Transit, Oxygen Matex 80+, E84-61 TunnelInformation provided by Applied Compos..
Compressive Strength	165 MPa	24000 psi	ASTM D695
Applied Composites 8050 Polyester SMC Industry Application: ElectricalProduct Application: Business MachinesDistinct Features: Radiant Panel, UL 94-VO, Low Shrink, PigmentableInformation provided by Applied Composites Corporation.
Compressive Strength	165 - 193 MPa	24000 - 28000 psi
Bulk Molding Compounds BMC 605LS Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 605LS molding compound is a low-shrink, mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is characterized by good mol..
Compressive Strength	165 - 193 MPa	24000 - 28000 psi
Bulk Molding Compounds BMC 610 - SP Mineral Filled, Glass Reinforced Polyester Compound, with UV Stabilizer BMC 610 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is set a part form other medium impact el..
Compressive Strength	165 - 193 MPa	24000 - 28000 psi
Bulk Molding Compounds BMC 610 Mineral filled, glass-fiber-reinforced polyester compound BMC 610 molding compound is a mineral filled, glass fiber reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is set a part form other medium impact..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced Polyester Flat Sheet 1/8" Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded products feature:High StrengthCorrosion Resistant to many che..
Compressive Strength	165 MPa	24000 psi	Lengthwise; ASTM D635
Bedford Plastics Glass Reinforced Polyester Flat Sheet, 3/8" to 1" Pultrusion results in the production and supply of one of the worlds strongest and most durable products available today. The pultruded products feature:High StrengthCorrosion Resistant to many che..
Compressive Strength	165 - 179 MPa	24000 - 26000 psi
Bulk Molding Compounds BMC 1412 Flame and Track Resistant BMC 1412 is an extremely versatile material. Flame and track resistant, low shrink for close dimensional control and surface smoothness, high physical properties. Developed for injection molding, bu..
Compressive Strength	165 - 193 MPa	24000 - 28000 psi
Bulk Molding Compounds BMC 5209-12940 Mineral Filled, Glass Reinforced Polyester BMC 5209-12940 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is a high impact material produced..
Compressive Strength	165 - 193 MPa	24000 - 28000 psi
Bulk Molding Compounds BMC 5338 Mineral Filled, Glass Reinforced Polyester BMC 5338 molding compound is a mineral Filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is a high impact material produced in ex..
Compressive Strength	165 - 193 MPa	24000 - 28000 psi
Bulk Molding Compounds BMC 605 Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 605 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is characterized by good moldability, medi..
Compressive Strength	165 - 193 MPa	24000 - 28000 psi
Bulk Molding Compounds BMC 610 Mineral Filled, Glass Reinforced Polyester Compound BMC 610 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is set a part form other medium impact el..
Compressive Strength	165 - 193 MPa	24000 - 28000 psi
Bulk Molding Compounds BMC 620M Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 620M molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, and stuffer injection molding It is characterized by high impact strength, good mol..
Compressive Strength	165.5 MPa	24000 psi
Henkel Hysol EA 9394/C-2 Paste Adhesive System Elevated cure, thixotropic adhesive with structural properties to 450°F / 232°C.Application: Structural Repair