Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | >= 10.0 MPa | >= 1450 psi | DIN 53504 |
NEXA® PFX8028 Perfluoroelastomer NEXA produces sealing elements for extreme and critical applications, particularly where high temperature, wet conditions (steam/water), purity and chemical resistance are important factors to consi.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | at Yield; ISO 527-1/-2 |
Quadrant EPP Fluorosint® 207 PTFE + mica, compression moulded (ISO Data) This material has a food contact compliant composition which, in combination with the good mechanical performance, dimensional stability, sliding and wear properties and inherent outstanding chemica.. |
|||
Tensile Strength | >= 10.0 MPa | >= 1450 psi | After 168 H in Air Oven at 100°C; NBR NM-IEC 60811-1-2 |
Karina Karintox 70/6 Polyolefin Compound Karintox is a thermoplastic polyolefin, flame retardant, non-halogen, and low smoke emission. Recommended for electrical coating for cables until 1KV. For a better usage/processing, manufacturer sug.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | DIN 53504/ISO 37 |
Kraiburg TPE THERMOLAST® K TC9CSN Thermoplastic Elastomer, Optimized compression set The CS Series is recommended for sealing applications, providing an excellent compression set. The compounds are available in natural and black colors. Typical applications: FasteningsGrommetsMembra.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | DIN 53504/ISO 37 |
Kraiburg TPE THERMOLAST® K TC9CSZ Thermoplastic Elastomer, Optimized compression set The CS Series is recommended for sealing applications, providing an excellent compression set. The compounds are available in natural and black colors. Typical applications: FasteningsGrommetsMembra.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | DIN 53504/ISO 37 |
Kraiburg TPE THERMOLAST® K TF5WKF Thermoplastic Elastomer, Drinking Water The DW Series is recommended for applications in contact with drinking water. The compounds are approved in accordance with all relevant European drinking water standards – DVGW, W270, KTW, WRA.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | DIN 53504/ISO 37 |
Kraiburg TPE THERMOLAST® K TF6THT Thermoplastic Elastomer, high transparency The FC/ht Series is a highly transparent material solution for applications with food contact. The series is characterized, among other things, by its excellent adhesion to PP. Typical applications:.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | DIN 53504/ISO 37 |
Kraiburg TPE THERMOLAST® K TP6HPN Thermoplastic Elastomer, Outdoor Grade Typical applications of the EX/UV Series: Edge guardsDistance ProfilesMolded Parts (Solar Equipment)SealsInformation Provided by Kraiburg TPE Corp. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | DIN 53504/ISO 37 |
Kraiburg TPE THERMOLAST® V TV8LVN Thermoplastic Elastomer, General purpose, long term performance The LTP Series is recommended for sealings requiring high temperature resistance. The compounds are characterized by an excellent adhesion to PP. Typical applications: FasteningsGrommetsSealsMateria.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
JPJ Technologies LD 150 LDPE Virgin Applications: Used for heavy duty packaging, packaging bags, general film bag, etc.Information provided by JPJ Technologies |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials Siloprenâ„¢ Electro 641 Electrically Insulating Liquid Silicone Rubber This LSR elastomer is an electrically insulating, two-component, platinum (addition/heat) curable, and pumpable silicone elastomer that can be molded and cured with very fast cycle times, at elevate.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials Siloprenâ„¢ LSR 2650 ZKS Custom Liquid Silicone Rubber - Automotive This LSR elastomer is a specialty grade, two-component, platinum (addition/heat) curable, and pumpable silicone elastomer that can be molded and cured with very fast cycle times, at elevated tempera.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials Siloprenâ„¢ LSR 2715/50 Liquid Silicone Rubber - Self-Bonding / Self-Lubricating This LSR elastomer is a self-bonding, self-lubricating, two-component, platinum (addition/heat) curable, and pumpable silicone elastomer that can be molded and cured with very fast cycle times, at e.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials Siloprenâ„¢ LSR 2740 Liquid Silicone Rubber - Self-Bonding This LSR elastomer is a self-bonding, two-component, platinum (addition/heat) curable, and pumpable silicone elastomer that can be molded and cured with very fast cycle times, at elevated temperatur.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials Siloprenâ„¢ LSR 2750 Liquid Silicone Rubber - Self-Bonding This LSR elastomer is a self-bonding, two-component, platinum (addition/heat) curable, and pumpable silicone elastomer that can be molded and cured with very fast cycle times, at elevated temperatur.. |
|||
Tensile Strength | >= 10.0 MPa | >= 1450 psi | ASTM D 638 |
Karina 806-40/236-H-ISE-LMP White PVC Compound Heavy metal free PVC compound.Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | >= 10.0 MPa | >= 1450 psi | After 168 H in Air Oven at 100°C; NBR NM-IEC 60811-1-2 |
Karina 806-40/236-H-ISE-LMP White PVC Compound Heavy metal free PVC compound.Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | >= 10.0 MPa | >= 1450 psi | After 168 H in Air Oven at 100°C; NBR NM-IEC 60811-1-2 |
Karina 807-10/236-H-Ise White PVC Compound Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials Silplusâ„¢ 80 EX Heat Cured Rubber - Extrusion Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Shin-Etsu Silicones LIMSâ„¢ KEG2002-60A/B Elastomer Information Provided by Shin-Etsu Silicones of America, Inc. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Master Bond EP30DPMed USP Class VI, Two Component Epoxy Urethane System Master Bond Polymer System EP30DPMED is a versatile, two component, epoxy-urethane elastomeric compound, featuring superior strength, toughness, and abrasion resistance for high performance bonding,.. |
|||
Tensile Strength | >= 10.0 MPa | >= 1450 psi | ASTM F152 |
Thermoseal RG-P160 PTG Gasketing Thermoseal RG-P160 is a blended fiber and polychloroprene rubber gasket material with mineral fillers. A factory applied release coating on both sides aid in flange removal. Continuous roll lengths .. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | ASTM D638 |
Goodfellow TPX® MX002O Polymethylpentene This grade is highly recommended for injection molding, film and mandrel extrusion; also for fiber extrusion and blow molding.TPX® is semi-crystalline, transparent, very light and - for a polyolefi.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | ASTM D638 |
Goodfellow TPX® DX310 Coating/Extrusion Grade Polymethylpentene This grade is highly recommended for paper coating or for fiber extrusion.TPX® is semi-crystalline, transparent, very light and - for a polyolefin - expensive. It has good release characteristics a.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | ASTM D412 |
Elastocon TPE Technologies Elastocon® CLR75 Thermoplastic Elastomer Elastocon® CLR75 is a transparent thermoplastic elastomer that has been developed for applications that require oil/plasticizer free, non-blooming high strength properties and a tactile surface fin.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | Silicone Property; ASTM D412 |
Arlon 99020N015 0.015" Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier Design/Construction:Interleave: 0.001" FEP FilmSide 1: Uncured Silicone RubberCarrier: 0.003" PTFE coated FiberglassRecommended Primer: Chemlock 607This data represents typical values for the pro.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | Silicone Property; ASTM D412 |
Arlon R35640T003 0.003" (0.0762 mm) Uncured Silicone Rubber with Polyethylene Naphthalate Substrate Design/Construction:Liner: Polyester Side 1: Uncured Silicone RubberSubstrate: Polyethylene NaphthalateAppearance: Gray gum on glass fiber fabricThis data represents typical values for the productio.. |
|||
Tensile Strength | >= 10.0 MPa | >= 1450 psi | ISO 37 |
Austin Novel Materials Texalan® 565A Polyether-based TPU Description: Good low temperature resistance, hydro resistance, which can be used in cold and humid temperaturesInformation from Dawnentech |
|||
Tensile Strength | 10.0 MPa | 1450 psi | 100; ISO 37 |
BASF Elastollan 890 AN TPUR Description: Thermoplastic Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, high tear and tensile strength, good damping characteristics and a high resilien.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials HV 3/706 Heat Cured Rubber - High Temperature Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |