Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 10.0 MPa | 1450 psi | at Yield; ISO 527-1/-2 |
Quadrant EPP Fluorosint® 207 PTFE + mica, compression moulded (ISO Data) This material has a food contact compliant composition which, in combination with the good mechanical performance, dimensional stability, sliding and wear properties and inherent outstanding chemica.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | ASTM D638 |
Quadrant EPP Fluorosint® HPV Mica-filled PTFE (ASTM Product Data Sheet) |
|||
Tensile Strength | 10.0 MPa | 1450 psi | at Yield; ISO 527-1/-2 |
Quadrant EPP Fluorosint® HPV PTFE + additives, bearing grade, compression moulded (ISO Data) FDA compliant Fluorosint HPV is a high performance Fluorosint bearing grade, optimized for high pressure-velocity capabilities and very low wear. Fluorosint HPV was developed for bearing application.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | at Yield; ISO 527-1/-2 |
Quadrant EPP Semitron® ESd 500HR PTFE, static dissipative, extruded (ISO Data) Reinforced with a proprietary synthetic mica, Semitron ESd 500HR offers an excellent combination of low frictional properties, good dimensional stability and electrostatic dissipation. Whenever virg.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | ISO 37 |
Kraton® D1163 J (SIS) Linear Block Copolymer Description: Kraton D1163 J Polymer is a clear, linear block copolymer based on styrene and isoprene with bound styrene of 15% mass. It is supplied from Japan in the physical form(s) identified in t.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials Addisilâ„¢ 1150 M Industrial Molding Heat Cured Rubber Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
JPJ Technologies LD 150 LDPE Virgin Applications: Used for heavy duty packaging, packaging bags, general film bag, etc.Information provided by JPJ Technologies |
|||
Tensile Strength | >= 10.0 MPa | >= 1450 psi | ASTM D 638 |
Karina 608-48/1-Y-IS-BZ Black PVC Compound Heavy metal free, weather resistant PVC Compound; recommended for injection and extrusion of automotive profiles.Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials Siloprenâ„¢ FFSL 7031 Fully Fluorinated Liquid Silicone Rubber This LSR elastomer is a fully fluorinated, two-component, platinum (addition/heat) curable, and pumpable silicone elastomer that can be molded and cured with very fast cycle times, at elevated tempe.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials Siloprenâ„¢ LSR 2650 Liquid Silicone Rubber - Fast Cure / High Tear This LSR elastomer is a general purpose, two-component, platinum (addition/heat) curable, and pumpable silicone elastomer that can be molded and cured with very fast cycle times, at elevated tempera.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials Siloprenâ„¢ LSR 2715/50 Liquid Silicone Rubber - Self-Bonding / Self-Lubricating This LSR elastomer is a self-bonding, self-lubricating, two-component, platinum (addition/heat) curable, and pumpable silicone elastomer that can be molded and cured with very fast cycle times, at e.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials Siloprenâ„¢ LSR 2750 Liquid Silicone Rubber - Self-Bonding This LSR elastomer is a self-bonding, two-component, platinum (addition/heat) curable, and pumpable silicone elastomer that can be molded and cured with very fast cycle times, at elevated temperatur.. |
|||
Tensile Strength | >= 10.0 MPa | >= 1450 psi | ASTM D 638 |
Karina 806-10/236-H-ISE White PVC Compound Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | >= 10.0 MPa | >= 1450 psi | After 168 H in Air Oven at 100°C; NBR NM-IEC 60811-1-2 |
Karina 806-10/236-H-ISE White PVC Compound Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | >= 10.0 MPa | >= 1450 psi | ASTM D 638 |
Karina 806-40/236-H-ISE-LMP White PVC Compound Heavy metal free PVC compound.Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials Siloprenâ„¢ LSR 4670 Liquid Silicone Rubber - Healthcare LSR elastomers are a two-component, platinum (addition/heat) curable, and pumpable silicone elastomer that can be molded and cured with very fast cycle times, at elevated temperatures. The molding .. |
|||
Tensile Strength | >= 10.0 MPa | >= 1450 psi | ASTM D 638 |
Karina 807-10/236-H-Ise White PVC Compound Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | >= 10.0 MPa | >= 1450 psi | After 168 H in Air Oven at 100°C; NBR NM-IEC 60811-1-2 |
Karina 807-10/236-H-Ise White PVC Compound Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials Siloprenâ„¢ LSR 7080 High Clarity Liquid Silicone Rubber This LSR elastomer is a specialty grade, two-component, platinum (addition/heat) curable, and pumpable silicone elastomer that can be molded and cured with very fast cycle times, at elevated tempera.. |
|||
Tensile Strength | >= 10.0 MPa | >= 1450 psi | ASTM F152 |
Thermoseal RG-P160 PTG Gasketing Thermoseal RG-P160 is a blended fiber and polychloroprene rubber gasket material with mineral fillers. A factory applied release coating on both sides aid in flange removal. Continuous roll lengths .. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | Silicone Property; ASTM D412 |
Arlon R35640T003 0.003" (0.0762 mm) Uncured Silicone Rubber with Polyethylene Naphthalate Substrate Design/Construction:Liner: Polyester Side 1: Uncured Silicone RubberSubstrate: Polyethylene NaphthalateAppearance: Gray gum on glass fiber fabricThis data represents typical values for the productio.. |
|||
Tensile Strength | >= 10.0 MPa | >= 1450 psi | ISO 37 |
Austin Novel Materials Texalan® 565A Polyether-based TPU Description: Good low temperature resistance, hydro resistance, which can be used in cold and humid temperaturesInformation from Dawnentech |
|||
Tensile Strength | 10.0 MPa | 1450 psi | 300; ISO 37 |
BASF Elastollan 2180 A TPUR Description: Thermoplastic Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, high tear and tensile strength, good damping characteristics and a high resilien.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | ASTM D412 |
Arlon RBLW401R##-P1 0.040" (1.02 mm) Cured Self-Fusing Silicone Rubber Description: 1 inch wide, 40 mil thick, Red, Triangular cross-section, Self-Fusing Silicone Tape. Product is supplied in various roll lengths. ## in the product number indicates roll length in yards.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | ASTM D412 |
Arlon RBLW401X##-P1 0.040" (1.02 mm) Cured Self-Fusing Silicone Rubber Description: 1 inch wide, 40 mil thick, Red, Triangular cross-section, Self-Fusing Silicone Tape. Product is supplied in various roll lengths. ## in the product number indicates roll length in yards.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials HV 3/706 Heat Cured Rubber - High Temperature Heat cured rubber is a high consistency product that can be molded, extruded or calendered using conventional rubber processing equipment to meet a wide range of cost, durability and performance sta.. |
|||
Tensile Strength | 10.0 MPa | 1450 psi | |
Momentive Performance Materials Silopren™ LSR 4060 Liquid Silicone Rubber - Healthcare LSR elastomers are a two-component, platinum (addition/heat) curable, and pumpable silicone elastomer that can be molded and cured with very fast cycle times, at elevated temperatures. The molding .. |
|||
Tensile Strength | 10.0 MPa @Strain 100 % |
1450 psi @Strain 100 % |
ISO 37 |
BASF Elastollan B 95 A TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, high tensile strength, good damping and resilience performance and sup.. |