Arlon R35640T003 0.003" (0.0762 mm) Uncured Silicone Rubber with Polyethylene Naphthalate Substrate

Category Polymer , Thermoset , Silicone , Silicone Rubber
Manufacturer Arlon
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon R35640T003 0.003" (0.0762 mm) Uncured Silicone Rubber with Polyethylene Naphthalate Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Liner: Polyester Side 1: Uncured Silicone RubberSubstrate: Polyethylene NaphthalateAppearance: Gray gum on glass fiber fabricThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
Physical Properties Metric English Comments
Thickness 25.4 microns
1.00 mil
Substrate; Arlon SQA-TMS-003
25.4 microns
1.00 mil
Liner
50.8 microns
2.00 mil
Side 1 rubber add-on; Arlon SQA-TMS-003
76.2 microns
3.00 mil
Overall; Arlon SQA-TMS-003
Mechanical Properties Metric English Comments
Hardness, Shore A 40
40
Silicone Property; ASTM D2240
Tensile Strength 10.0 MPa
1450 psi
Silicone Property; ASTM D412
Elongation at Break 850 %
850 %
Silicone Property; ASTM D412
Peel Strength 1.75 kN/m
10.0 pli
Bond Strength; ASTM D624
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 163 °C
325 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Electrical Properties Metric English Comments
Dielectric Strength 78.7 kV/mm
2000 kV/in
ASTM D149
Processing Properties Metric English Comments
Cure Time 10.0 min

@Pressure 0.345 MPa,
Temperature 163 °C
0.167 hour

@Pressure 50.0 psi,
Temperature 325 °F
Recommended Cure Cycle
Shelf Life 3.00 Month

@Temperature 4.44 °C
3.00 Month

@Temperature 40.0 °F
From date of manufacture
Descriptive Properties Value Comments
Color Translucent (Natural)
Total Product Weight (oz/yd2) 2.7
Arlon SQA-TMS-025