Solvay Specialty Polymers Udel® GF-130 Polysulfone (PSU)  (Unverified Data**)

Category Polymer , Thermoplastic , Polysulfone (PSU) , Polysulfone, 10% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Udel® GF-130 Polysulfone (PSU)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Udel GF-130, resin is a 30% glass fiber reinforced polysulfone compound. Glass fiber substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical resistance of the polysulfone resin. The high performance properties and attractive price make these resins particularly effective alternatives to metals in many engineering applications. - Black: Udel GF-130 BK 937 - Natural: Udel GF-130 NTInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Specific Gravity 1.49 g/cc
1.49 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ASTM D955
Melt Flow 6.5 g/10 min

@Load 2.16 kg,
Temperature 343 °C
6.5 g/10 min

@Load 4.76 lb,
Temperature 649 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength 108 MPa
15700 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ASTM D638
Tensile Modulus 8.69 GPa
1260 ksi
ASTM D638
Flexural Strength 154 MPa
22300 psi
ASTM D790
Flexural Modulus 7.58 GPa
1100 ksi
ASTM D790
Izod Impact, Notched 0.690 J/cm
1.29 ft-lb/in
ASTM D256
Tensile Impact Strength 113 kJ/m²
53.8 ft-lb/in²
ASTM D1822
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 181 °C
358 °F
Unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 3.18 mm
V-0

@Thickness 0.125 in
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+16 ohm-cm
2.00e+16 ohm-cm
ASTM D257
Dielectric Constant 3.47

@Frequency 1.00e+6 Hz
3.47

@Frequency 1.00e+6 Hz
ASTM D150
3.48

@Frequency 60.0 Hz
3.48

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 19.0 kV/mm
483 kV/in
ASTM D149
Dissipation Factor 0.00070

@Frequency 60.0 Hz
0.00070

@Frequency 60.0 Hz
ASTM D150
0.0050

@Frequency 1.00e+6 Hz
0.0050

@Frequency 1.00e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Melt Temperature 343 - 399 °C
649 - 750 °F
Mold Temperature 121 - 163 °C
250 - 325 °F
Drying Temperature 163 - 191 °C
325 - 376 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi
Descriptive Properties Value Comments
Agency Ratings ISO 10993
ISO 10993-Part 1
NSF 61
Tested at 82 °C (180 °F) (Commercial Hot)
Appearance Black
Natural Color
Opaque
Availability Asia Pacific
Europe
North America
South America
Features Acid Resistant
Alcohol Resistant
Alkali Resistant
Good Chemical Resistance
Good Creep Resistance
Good Dimensional Stability
Good Strength
High Heat Resistance
High Rigidity
Hydrocarbon Resistant
Hydrolytically Stable
Filler Glass Fiber Reinforcement
Forms Pellets
Generic PSU
Injection Rate Fast
Processing Method Extrusion
Injection Molding
RoHS Compliance RoHS Compliant
Screw Compression Ratio 2.0:1.0
Uses Appliance Components
Appliances
Automotive Electronics
Electrical Parts
Electrical/Electronic Applications
Food Service Applications
Industrial Parts
Microwave Cookware
Piping
Plumbing Parts
Valves/Valve Parts
Copyright © lookpolymers.com All Rights Reserved