Polymer Property : Melt Flow = 0.35 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 230 °C	0.35 g/10 min @Load 4.76 lb, Temperature 446 °F	Condition L; ASTM D1238
PolyMirae Moplen EP332C Pipe Extrusion Grade Polypropylene Moplen EP332C is the polypropylene block copolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen EP332C is a block copolymer appreciated by customers in the mar..
Melt Flow	0.35 g/10 min	0.35 g/10 min	ExxonMobil Method
ExxonMobil Escorene® LD 712.06 Film Resin (discontinued **) Escorene Ultra LD 712 series is a fraction melt index, 10 wt% vinyl acetate copolymer specialty film resin for applications requiring outstanding heat sealability, strength and toughness, particular..
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 190 °C	0.35 g/10 min @Load 4.76 lb, Temperature 374 °F	Condition E; ASTM D1238
Global G-2855 High Density Polyethylene, Blow Molding Grade (discontinued **) Description-opacity, medium high stiffness, good impact strength, good chemical resistanceApplications- auto parts, bottles, housewares, drums, containers, bottlesMeets FDA requirements as listed in..
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 230 °C	0.35 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
Phillips 66 COPYLENE® CM003P Polypropylene Impact Copolymer COPYLENE® CM003P is a fractional melt flow impact copolymer with a barefoot additive package which is specially formulated to excel in extrusion processes.Applications: Extrusion ProcessesInformati..
Melt Flow	0.35 g/10 min @Load 5.00 kg, Temperature 190 °C	0.35 g/10 min @Load 11.0 lb, Temperature 374 °F	ASTM D1238
Braskem ES 300 HDPE Blown Film Extrusion Polyethylene (discontinued **) 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Grocery and T-shirt bags; merchandise bags; frozen-food bags; high-strength films. Informa..
Melt Flow	0.35 g/10 min	0.35 g/10 min	ASTM D1238
LyondellBasell PetrotheneÂ® LB5604 High Density Polyethylene ApplicationsThe PETROTHENE LB 5604 series of polyethylene resins exhibits good stiffness and environmental stress cracking resistance. Typical applications include household chemical and person car..
Melt Flow	0.35 g/10 min	0.35 g/10 min	ASTM D1238
LyondellBasell PetrotheneÂ® LB560401 High Density Polyethylene ApplicationsPetrothene LB560401 exhibits good stiffness and environmental stress crack resistance. Typical applications include household chemical and personal care product bottles.Regulatory Status..
Melt Flow	0.35 g/10 min	0.35 g/10 min	ASTM D1238
LyondellBasell PetrotheneÂ® LM600500 High Density Polyethylene ApplicationsPETROTHENE LM 6005-00 resin is especially designed for water, milk, and juice bottles. It exhibits excellent rigidity and good processability.Regulatory StatusLM 6005-00 meets the requi..
Melt Flow	0.35 g/10 min	0.35 g/10 min	ASTM D1238
I. Stern IS-35955 High Density Polyethylene, Blow Molding Grade Features:IS-35955 is designed for applications requiring excellent stiffness and stress crack resistance properties.Meets all requirements of the U. S. Food and Drug Administration as specified in 2..
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 190 Â°C	0.35 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238
Ineos B50-35H-011 HDPE Ineos B50-35H-011 is a high density polyethylene copolymer developed for blow molding applications. It is recommended for use in applications which require a combination of high top load strength a..
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 230 Â°C	0.35 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ISO 1133
Inno-Comp INNOPOLÂ® CS 5-8250 W 50% Chalk-Filled High Density Polyethylene INNOPOLÂ® CS 5-8250 W is a 50% chalk-filled compound based on high density polyethylene.INNOPOLÂ® CS 5-8250 W is developed for packaging film production.All information provided by INNO-COMP.
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 190 Â°C	0.35 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238
Iran Petrochemical (PCC) HB0035 High Density Polyethylene HB0035 is a high molecular weight high density polyethylene blow molding grade combining blow molding extrusion behavior and superior mechanical properties. Blow molded items made from HB 0035 exhi..
Melt Flow	0.35 g/10 min	0.35 g/10 min
JPJ Technologies 6600B HDPE Blow Molding Information provided by JPJ Technologies
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 190 Â°C	0.35 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238
Solvay Specialty Polymers PolidanÂ® EC/51 Polyethylene, Crosslinked (XLPE) Flexible low density polyethylene based compound crosslinkable by moisture; it consists of a silane pregrafted base compound (SioplasÂ® method) to be used with a catalyst masterbatch.Standards com..
Melt Flow	0.35 g/10 min @Load 2.16 kg	0.35 g/10 min @Load 4.76 lb	ISO 1133
SIDPEC EGYPTENEÂ® HD 5403 EA HDPE Blow Molding Applications:Blow molded containers up to 30 liters for packagingChemicalsHousehold productsOils and foodstuffsInformation provided by Interchim s.r.l., official distributor of Sidi Kerir Petrochemi..
Melt Flow	0.35 g/10 min	0.35 g/10 min	Condition not noted.; ASTM D1238
DuPont Elvax® 3135X Ethylene-Vinyl Acetate Copolymer Resin for Thin Blown 12 wt% Vinyl Acetate.Elvax® 3135X is an extrudable, ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene resi..
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 190 °C	0.35 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238, ISO 1133
DuPont Elvax® 670 Ethylene Vinyl Acetate DuPont™ Elvax® 670 is an ethylene-vinyl acetate copolymer resin for use in industrial applications.Applications:Elvax® 670 resins can be used for the following applications: molding, compounding ..
Melt Flow	0.35 g/10 min @Load 2.16 kg	0.35 g/10 min @Load 4.76 lb	ASTM D 1238
Total 5202 HDPE, blow molding Applications: Bleach and detergents, industrial chemicals, industrial parts, packaging aggressive liquids, food packaging. Blow molding stock temperature 360 - 400°F Extrusion melt temperature 380 ..
Melt Flow	0.35 g/10 min @Load 2.16 kg	0.35 g/10 min @Load 4.76 lb	ASTM D 1238
Total 5502 BZ HDPE injection blow molding Applications: Cosmetics and toiletries, pharmaceuticals, specialty containers, food packagingInformation provided provided by Total Petrochemicals.Total Petrochemicals acquired former Fina and Atof..
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 190 °C	0.35 g/10 min @Load 4.76 lb, Temperature 374 °F	Condition E; ASTM D1238
Formosa Plastics Formolene® HB5502A Blow Molding HDPE High Density Polyethylene Hexene Copolymer for Blow Molding – With Antistat Formolene® HB5502A is designed for applications requiring excellent stiffness and stress crack resistance properties. It..
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 190 °C	0.35 g/10 min @Load 4.76 lb, Temperature 374 °F	Condition E; ASTM D1238
Formosa Plastics Formolene® HB5502F Blow Molding HDPE High Density Polyethylene Hexene Copolymer with Synthetic Antistat Formolene® HB5502F HDPE resin is designed for applications requiring excellent stiffness and stress crack resistance properties. I..
Melt Flow	0.35 g/10 min	0.35 g/10 min	ASTM D1238
ExxonMobil Nexxstar™ NX-00328 Low Density Polyethylene Resin Product Description: Nexxstar 00328 is an LDPE grade, which offers good film rigidity combined with very good optical properties. Its primary use is for high performance collation shrunk packaging.A..
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 190 °C	0.35 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Entec Hypel® PEHD.3/.955 HDPE Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ente..
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 190 °C	0.35 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Borealis LE6025 Polyethylene Modified Jacketing Compound LE6025 is a black low density copolymer modified polyethylene compound. It is characterized by excellent stress crack resistance and mechanical properties and low temperature performance in combinat..
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 190 °C	0.35 g/10 min @Load 4.76 lb, Temperature 374 °F	Condition E; ASTM D1238
Formosa Plastics Formolene® HB5502B2 Blow Molding HDPE Hexene CopolymerApplications: Pharmaceutical Packaging; Personal Care Products; Bleach and Detergents Industrial; and Chemicals & PartsFormolene® HB5502B2 is designed for applications requiring ex..
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 190 °C	0.35 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238, ISO 1133
DuPont Elvax® 3135B Ethylene Vinyl Acetate (discontinued **) DuPont™ Elvax® 3135B is an extrudable ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene resins. Additive:..
Melt Flow	0.35 g/10 min	0.35 g/10 min	Exxon Method (I2). HLMI (I21) is 20 g/10 min.
ExxonMobil Escorene® HD-7835 MMW-HDPE Blown Film Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.A medium molecular weight HDPE blown film resin. Films made from the HD-7835 exhibit an excellent stiffness balance. HD-7835 is particularly recom..
Melt Flow	0.35 g/10 min	0.35 g/10 min	ASTM D1238
LyondellBasell Alathon® 9301 High Density Polyethylene ApplicationsALATHON 9301is a high density resin designed for sheet extrusion and thermoforming. It exhibits very low sag and high stiffness.Regulatory StatusALATHON 9301 meets the requirements of F..