SABIC Innovative Plastics Lexan® HP9NR PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® HP9NR PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. For blow molding applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 | |
| Water Absorption | 0.15 % @Time 86400 sec |
0.15 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 |
| Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | ASTM D570 |
| 0.58 % @Temperature 100 °C |
0.58 % @Temperature 212 °F |
ASTM D570 | |
| Water Absorption at Saturation | 0.26 % | 0.26 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 2.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 2.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 62.0 MPa | 8990 psi | 50 mm/min; ISO 527 |
| 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 |
| 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ISO 527 |
| 110 % | 110 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 6.8 % | 6.8 % | 50 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.13 GPa | 309 ksi | 5 mm/min; ASTM D638 |
| 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 93.0 MPa | 13500 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min; ISO 178 |
| 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 7.47 J/cm | 14.0 ft-lb/in | ASTM D256 |
| 1.36 J/cm @Temperature -30.0 °C |
2.55 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 32.04 J/cm | 60.02 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 54.0 kJ/m² | 25.7 ft-lb/in² | 80*10*4; ISO 180/1A |
| 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 7.20 J/cm² | 34.3 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 169 J | 125 ft-lb | ASTM D3029 |
| 77.0 J @Temperature 23.0 °C |
56.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 | |
| Taber Abrasion, mg/1000 Cycles | 10 | 10 | CS-17, 1 kg; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.4 µm/m-°C @Temperature -40.0 - 95.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Specific Heat Capacity | 1.25 J/g-°C | 0.299 BTU/lb-°F | ASTM C351 |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C | 268 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 132 °C @Thickness 6.40 mm |
270 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 157 °C | 315 °F | Rate B/50; ASTM D1525 |
| 160 °C | 320 °F | Rate B/50; ISO 306 | |
| 162 °C | 324 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 0.450 mm |
HB @Thickness 0.0177 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.586 | 1.586 | ASTM D542 |
| Haze | 1.0 % @Thickness 2.54 mm |
1.0 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 88 % | 88 % | 2.54 mm; ASTM D1003 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Specific Volume | 0.83cm^3/g | ASTM D792 |
Users viewing this material also viewed the following:
- Pau Tai Unistab BT-18A Organotin Stabilizer Butyl/Octyl Carboxylate Tin
- Lehmann & Voss LUVOCOM® 80-7713 Polyacetal-copolymer, with carbon fiber and PTFE
- Iran Petrochemical (PCC) I4 HD 7255 High Density Polyethylene
- Mitsui Arlenâ„¢ A335 35% Glass Fiber-Reinforced Modified Nylon 6T (COND)
- SABIC Innovative Plastics LNP LUBRICOMP RN001S PA 66 (Asia Pacific)
- Techmer ES HiFill® PA6 GF50 LE 50% Glass Filled (Dry)
- Silberline Silcroma® BG-13
- ExxonMobil PP7694E2 Impact Copolymer
- Eurotec® Tecodur® PB70 GR10 NL100 PBT, 10% glass fiber reinforced, natural
- A. Schulman POLYBATCH™ Metallic Grey 80330/2
Copyright © lookpolymers.com All Rights Reserved