Polymer Property : Linear Mold Shrinkage, Transverse = 0.0030 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ASTM D955
PolyOne LubriOne™ CTX-502 Natural Polyether Imide (PEI)
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
SABIC Innovative Plastics Lexan® HFD4413 PC (Asia Pacific)
Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
Linear Mold Shrinkage, Transverse 0.00090 - 0.0030 cm/cm
0.00090 - 0.0030 in/in
ASTM D955
PolyOne Edgetek® UR2-40CF/000 BLACK Polyurethane, Unspecified (PUR, Unspecified)
The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for ..
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
SABIC Innovative Plastics Lexan® LGK5030 PC (Asia Pacific)
Glass reinforced. Flame retardant.
Linear Mold Shrinkage, Transverse 0.0020 - 0.0030 cm/cm
0.0020 - 0.0030 in/in
Test Condition: 60x60x2; ISO 294-4
Ineos ABS Lustran® ABS 150G22 20% Glass Fiber Reinforced Grade
Linear Mold Shrinkage, Transverse 0.0015 - 0.0030 cm/cm
0.0015 - 0.0030 in/in
LATI Larton GCE/600 PPS, Glass/Mineral Reinforced
Polyphenylene Sulfide (PPS) based compound. Glass fibers / Mineral filler. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa ..
Linear Mold Shrinkage, Transverse 0.0015 - 0.0030 cm/cm
0.0015 - 0.0030 in/in
LATI Larton GCE/650 PPS, Glass/Mineral Reinforced
Polyphenylene Sulfide (PPS) based compound. Glass fibers / Mineral filler. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa ..
Linear Mold Shrinkage, Transverse 0.0020 - 0.0030 cm/cm
0.0020 - 0.0030 in/in
LATI Larton K/20 PPS, 20% Carbon Fiber Reinforced
Polyphenylene Sulfide (PPS) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; As..
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
Lanxess Durethan® ECO BV 30 H2 900500 Nylon 6, 30% Glass Fiber
PA 6, 30% glass fibers, injection molding, heat-ageing stabilized, contains 30% pre-consumer recycled materialInformation provided by LANXESS.
Linear Mold Shrinkage, Transverse 0.0020 - 0.0030 cm/cm
0.0020 - 0.0030 in/in
LATI Larton L K/20 L-PPS, 20% Carbon Fiber Reinforced
Linear Polyphenylene Sulfide (L-PPS) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle..
Linear Mold Shrinkage, Transverse 0.0015 - 0.0030 cm/cm
0.0015 - 0.0030 in/in
LATI Laticonther 80 GCE/650 PPS, Glass/Mineral Reinforced
High thermal conductivity product based on Polyphenylene Sulfide (PPS). Glass fibers / Mineral filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformatio..
Linear Mold Shrinkage, Transverse 0.0015 - 0.0030 cm/cm
0.0015 - 0.0030 in/in
LATI Latilon 28D K/40 PC, 40% Carbon Fiber Reinforced
Polycarbonate (PC) based compound. Carbon fiber. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided b..
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
SABIC Innovative Plastics LNP STAT-KON DX10315C PC (Asia Pacific)
LNP* Stat-Kon* DX10315C is carbon fiber filled polycarbonate composite with good stiffness, good flow ability, ESD safety, and high level of cleanliness for the most demanding application. This comp..
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP STAT-KON DX13320C PC COPOLYMER (Asia Pacific)
LNP* Statkon DX13320C is ultra clean polycarbonate/carbon fiber compound with high modulus, good flow ability, easy mold release, and high level of cleanliness for the most demanding application. A ..
Linear Mold Shrinkage, Transverse 0.0020 - 0.0030 cm/cm

@Time 86400 sec
0.0020 - 0.0030 in/in

@Time 24.0 hour
ASTM D 955
SABIC Innovative Plastics LNP Stat-kon EE008E PEI (Asia Pacific)
LNP STAT-KON* EE008E is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Asia Pacif..
Linear Mold Shrinkage, Transverse 0.0020 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Europe-Africa-Middle East)
LNP* Stat-kon* Lexan_LCF1506 is a 15% carbon fiber, 6% PTFE reinforced polycarbonate.
Linear Mold Shrinkage, Transverse 0.0015 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0015 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC1010 PPE+HIPS (Europe-Africa-Middle East)
LNP* Stat-kon* HMC1010 compound is a 10% Carbon fiber reinforced. Static dissipative. Nonbrominated, nonchlornated flame retardant system. UL94 V-1 rated.
Linear Mold Shrinkage, Transverse 0.0015 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0015 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC1010 PPE+PS
LNP* Stat-kon* Noryl_HMC1010 compound is a 10% Carbon fiber reinforced. Static dissipative. Nonbrominated, nonchlor- nated flame retardant system. UL94 V-1 rated.
Linear Mold Shrinkage, Transverse 0.0015 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0015 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC3008A PPE+HIPS (Europe-Africa-Middle East)
LNP* Stat-kon* Noryl_HMC3008A compound is a 30% glass/mineral/carbon fiber reinforced resin; static dissipative; 250F (120C) HDT. Tight tolerance molding.
Linear Mold Shrinkage, Transverse 0.0015 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0015 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
SABIC Innovative Plastics LNP STAT-KON Noryl_HMC3008A PPE+PS
LNP* Stat-kon* Noryl_HMC3008A compound is a 30% glass/mineral/carbon fiber reinforced resin; static dissipative; 250F (120C) HDT. Tight tolerance molding.
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP D351 PC (Asia Pacific)
LNP* Thermocomp* D351 (experimental grade name as EXTC8143) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus,..
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP EXTC8143 PC (Asia Pacific)
LNP* Thermocomp* EXTC8143 is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good ductility, No..
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK5030 PC
LNP* Thermocomp* Lexan_LGN5030 compound is a glass reinforced. Flame retardant.
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK5030 PC (Asia Pacific)
Glass reinforced. Flame retardant.
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
SABIC Innovative Plastics LNP THERMOCOMP Lexan_LGK5030 PC (Europe-Africa-Middle East)
LNP* Thermocomp* Lexan_LGK5020 compound is a glass reinforced, flame retardant material.
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
SABIC Innovative Plastics Lexan® HFD4412 PC
Lexan* HFD4412 is a 20% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
SABIC Innovative Plastics Lexan® HFD4413 PC (Europe-Africa-Middle East)
Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
Linear Mold Shrinkage, Transverse 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
SABIC Innovative Plastics Lexan® HFD4412 PC (Asia Pacific)
Lexan* HFD4412 is a 20% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
Linear Mold Shrinkage, Transverse 0.0020 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Asia Pacific)
15% carbon fiber, 6% PTFE reinforced polycarbonate.