Material Notes:
Product description: Grivory GCL-3H anthracite is based on a combination of a heat stabilized semi-crystalline Polyamide with a partially aromatic Polyamide. The product is reinforced by 30% long carbon fibers. Grivory GCL-3H anthracite is characterized by the following key-properties: very high stiffness and strength even after conditioning and over a wide temperature rangeexcellent notched impact resistance also at low temperatureslow creephigh heat distortion temperatureslow moisture absorptionvery good dimensional stability and little warpagevery little coefficient of thermal expansionvery low density Grivory The product has been designed for injection molding of technical parts especially in the area of light weight metal and composite replacement. Grivory GCL-3H anthracite is used in the following market segments: sports & leisureautomotivemechanical engineering The carbon fibers are aligned in parallel and are just as long as the pellets (usually 10 mm).Information provided by EMS Grivory
Physical Properties Metric English Comments
Density 1.28 g/cc
0.0462 lb/in³
ISO 1183
Water Absorption 4.7 %
4.7 %
ISO 62
Moisture Absorption 1.50 %
1.50 %
ISO 62
Linear Mold Shrinkage, Transverse 0.0010 cm/cm
0.0010 in/in
ISO 294-4, 2577
Mechanical Properties Metric English Comments
Ball Indentation Hardness 285 MPa
41300 psi
conditioned; ISO 2039-1
320 MPa
46400 psi
dry; ISO 2039-1
Tensile Strength at Break 215 MPa
31200 psi
dry; ISO 527-1/-2
270 MPa
39200 psi
conditioned; ISO 527-1/-2
Elongation at Break 1.6 %
1.6 %
dry; ISO 527-1/-2
1.7 %
1.7 %
conditioned; ISO 527-1/-2
Tensile Modulus 21.5 GPa
3120 ksi
conditioned; ISO 527-1/-2
22.5 GPa
3260 ksi
dry; ISO 527-1/-2
Charpy Impact Unnotched 5.50 J/cm²
26.2 ft-lb/in²
dry; ISO 179/1eU
6.50 J/cm²
30.9 ft-lb/in²
conditioned; ISO 179/1eU
5.50 J/cm²

@Temperature 30.0 °C
26.2 ft-lb/in²

@Temperature 86.0 °F
dry; ISO 179/1eU
6.50 J/cm²

@Temperature 30.0 °C
30.9 ft-lb/in²

@Temperature 86.0 °F
conditioned; ISO 179/1eU
Charpy Impact, Notched 1.60 J/cm²
7.61 ft-lb/in²
dry; ISO 179/1eA
1.60 J/cm²
7.61 ft-lb/in²
conditioned; ISO 179/1eA
2.00 J/cm²

@Temperature 30.0 °C
9.52 ft-lb/in²

@Temperature 86.0 °F
dry; ISO 179/1eU
2.00 J/cm²

@Temperature 30.0 °C
9.52 ft-lb/in²

@Temperature 86.0 °F
conditioned; ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 µm/m-°C
5.56 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 25.0 µm/m-°C
13.9 µin/in-°F
ISO 11359-1/-2
Melting Point 260 °C
500 °F
10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air 100 - 120 °C
212 - 248 °F
long term; EMS
220 °C
428 °F
short term; EMS
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 240 °C
464 °F
ISO 75-1/-2
Flammability, UL94 HB
HB
IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 3000 ohm-cm
3000 ohm-cm
dry; IEC 60093
3000 ohm-cm
3000 ohm-cm
conditioned; IEC 60093
Surface Resistance 50 ohm
50 ohm
IEC 60093
Descriptive Properties Value Comments
Automotive Automotive electr. and electronics, lighting
Cooling and climate control
Exterior
Fuel systems
Interior
Powertrain and Chassis
Electricals & Electronics Connectors
Electrical appliances
Electrical equipment
Energy distribution
Form Granules
Industry & Consumer goods Housewares
Hydraulics & Pneumatics
Mechanical Engineering
Power transmission
Sports & Leisure
Tools & Accessories
Processing Injection Molding
Product Attributes Long Fiber Reinforced
Special Characteristics Anti-static
Improved heat resistance